Disertación de Maestría
DOI
10.11606/D.23.2009.tde-19122009-122056
Documento
Autor
Nombre completo
Taciana Emília de Almeida Anfe
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2009
Director
Tribunal
Vieira, Glauco Fioranelli (Presidente)
Agra, Carlos Martins
Bittencourt, Edison
Título en portugués
Avaliação da possiibilidade de remoção do manchamento de resinas compostas submetidas ao envelhecimento artificial através do re-polimento
Palabras clave en portugués
Manchamento
Re polimento
Resina composta
Resumen en portugués
Nesta pesquisa in vitro verificou-se a possibilidade de remoção do manchamento causado por café ou vinho tinto em cinco resinas compostas disponíveis comercialmente, após serem submetidas ao processo de envelhecimento. Trinta e seis espécimes de cada resina composta foram confeccionados em uma matriz de teflon, com 10 mm de diâmetro e 1,5 mm de espessura. Os espécimes foram mantidos em água destilada a 37ºC por 24 horas e, em seguida, polidos com irrigação na politriz (Ecomet Buehler USA) nas duas superfícies, com lixa de carbureto de silício com granulação de número 600, até atingirem a espessura de 1,3 ±0,01 mm. Após o polimento, a cor dos espécimes foi aferida com espectrofotômetro Cintra 10 UV (Visible Spectrometer, GBC, Austrália). Todos os espécimes foram submetidos à ciclagem térmica com temperaturas de 5 e 55ºC, com tempo de imersão de 1 minuto, por 1000 ciclos em solução de 75% álcool-água. Após a ciclagem térmica, os espécimes foram mantidos imersos em água destilada a 37ºC até completar o período de 7 dias da confecção das amostras. Após esse período, todos os espécimes foram levados ao espectrofotômetro para leitura da cor. Os espécimes foram divididos em três grupos, cada um com n=12, de acordo com as soluções em que foram imersos: água destilada (controle), café e vinho tinto. Para que o processo de manchamento acontecesse em uma única superfície do espécime, uma das faces e a superfície lateral do espécime foram isoladas com cera branca. Os espécimes foram imersos nas diferentes soluções e mantidos a 37ºC por 14 dias. Após o período de manchamento, a cera foi removida e a superfície submetida ao manchamento passou por escovação com escova elétrica (Escova Elétrica Braun Oral-B Procter & Gamble do Brasil S.A., Manaus, Brasil) por 30 segundos com pressão leve. Os espécimes foram secos com papel absorvente e novamente levados ao espectrofotômetro para medição da cor. Em seguida, os espécimes foram submetidos a três desgastes de 20 m e a cor foi aferida após cada um dos desgastes. O cálculo da diferença de cor foi realizado através da fórmula CIEDE2000. De acordo com a metodologia utilizada neste estudo, concluiuse que o manchamento provocado por café e vinho tinto nos compósitos avaliados foi superficial e um desgaste de 20 m foi suficiente para remoção de tal manchamento.
Título en inglés
Evaluation of the remove possibility of composite resin staining submitted to artificial aging through repolishing
Palabras clave en inglés
Composite resin
Repolishing
Staining
Resumen en inglés
This in vitro research verified the possible elimination of staining caused by coffee and red wine in five commercial composite resins, after being submitted to thermal cycling. Thirty six specimens were prepared in a teflon mold with 10 mm in diameter and 1.5 mm thick. The specimens were immersed in water at 37ºC for 24 h and polished (Ecomet Buehler - USA) in both surfaces with a # 600 grit silicon carbide paper until achieve 1.3 ±0.01 mm thickness. After polishing, specimens color was measured in a spectrophotometer Cintra 10 UV (Visible Spectrometer, GBC, Austrália). All specimens were submitted to thermal cycling with temperatures of 5 and 55ºC with a dwell time of 1 minute, for 1000 cycles in a 75% ethanol/water solution. After thermal cycling the specimens were immersed in water at 37ºC until complete 7 days from the preparation of the specimens. All the specimens were then taken into spectrophotometer for measuring the color. The specimens were divided into 3 groups (n=12): distilled water (control), coffee and red wine. For the purpose of the staining process to occur in only one surface, all the side and one of the surfaces were isolated with white wax. The specimens were immersed in one of the solutions at 37ºC for 14 days. After the staining period, the wax was removed and the specimens were brushed with electric toothbrush (Braun Oral-B, Procter & Gamble do Brasil S.A., Manaus, Brasil) for 30 seconds with a slight pressure. The specimens were dry with a tissue paper and were taken to spectrophotometer for measuring the color. Following, the specimens were submitted to three wears of 20 m and the color was measured after each one of the wears. The calculation of the color difference was made through CIEDE2000 formula. According to the methodology used in this research, it was concluded that the staining caused by coffee and red wine was superficial and one wear of 20 m was enough for removing the discoloration.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-01-28
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.