Tesis Doctoral
DOI
10.11606/T.23.2008.tde-21012009-143919
Documento
Autor
Nombre completo
Bruno Lopes da Silveira
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2008
Director
Tribunal
Eduardo, Carlos de Paula (Presidente)
Aranha, Ana Cecilia Corrêa
Francischone, Carlos Eduardo
Soares, Sheila Cynthia Gouw
Valandro, Luiz Felipe
Título en portugués
Avaliação in vitro da resistência adesiva e degradação da interface de união entre cimentos resinosos e uma cerâmica aluminizada tratada internamente com laser
Palabras clave en portugués
Cerâmica
Hipoclorito de sódio
Laser de Nd:YAG
Microtração
Óxido de alumínio
Rocatec
Resumen en portugués
O estudo teve o objetivo de avaliar a resistência adesiva e a degradação da interface entre uma cerâmica tratada com laser e cimentos resinosos. Sessenta e quatro blocos cerâmicos foram distribuídos em 16 grupos distribuídos de acordo com os fatores em estudo: tratamento da superfície interna da cerâmica: Oxido de Alumínio (Ox), Rocatec (R), Laser de Nd:YAG 141,54 J/cm2 (Nd) e Laser de Nd:YAG + Rocatec (NdR); cimentos resinosos: Panavia F (Kuraray) e Relyx Unicem (3M ESPE); e método de envelhecimento: água destilada (W) e hipoclorito de sódio 10% (H). Após os procedimentos de cimentação e corte dos blocos, metade dos palitos foi armazenada em solução de hipoclorito de sódio 10% para simular envelhecimento in vitro. A resistência de união foi avaliada através do ensaio de microtração (0,5 mm/min) e os padrões de fratura foram classificados em adesivo, coesivo ou misto. Blocos cerâmicos adionciais foram confeccionados e analisados em Microscopia Eletrônica de Varredura e em Microscópio de Força Atômica para verificação dos padrões gerados pelos tratamentos. Os grupos tratados com laser de Nd:YAG apresentaram os maiores valores de resistência de união. Para os grupos cimentados com Panavia F, os valores de resistência de união foram: OxW: 27,71±6,3; RW: 35,67±5,13; NdW: 42,49±6,8; NdRW: 37,41±4,76; OxH: 22,27±6,05; RH: 27,49±8,83; NdH: 32,24±6,94; NdRH: 31,75±7,77. Para os grupos com RelyX Unicem: OxW: 26,74±6,34; RW: 35,07±6,02; NdW: 41,05±7,71; NdRW: 33,85±6,03; OxH: 22,77±7,37; RH: 27,84±6,26; NdH: 36,42±5,08; NdRH: 27,6±5,8. Pode-se concluir que o laser de Nd:YAG foi o tratamento mais efetivo, seguido da associação entre o laser de Nd:YAG+Rocatec, Rocatec e jateamento com Al2O3. Os cimentos testados apresentam comportamentos similares. O envelhecimento in vitro com hipoclorito de sódio diminuiu os valores de resistência de união.
Título en inglés
In Vitro analsis of bond strength and degradation method between bond interface of aluminous ceramic and resin cements
Palabras clave en inglés
Aluminum oxide sandblasting
Ceramic
Microtensile test
Nd:YAG laser
Rocatec
Sodium hypochlorite
Resumen en inglés
The aim of this study was to evaluate the influence of different surface treatments on resistance to degradation between In-Ceram Alumina and two resin-based cements. Sixteen experimental groups were formed according to ceramic treatment: Sandblasting (S), Rocatec System (R), Nd:YAG Laser (Nd), Nd:YAG Laser plus Rocatec System (NR); luting cement: Panavia F (Kuraray) or Relyx Unicem (3M ESPE); and aging method: water (W) or sodium hypochlorite (H). Sixty four In-Ceram Alumina blocks (10x10x6mm) received four surface treatments: Al2O3 sandblasting; Al2O3 sandblasting + Rocatec Plus; Al2O3 sandblasting + Nd:YAG Lase; Al2O3 sandblasting + Nd:YAG Laser + Rocatec Plus. Each conditioned ceramic block was bonded to a composite block using a resin cement system. After 24h storage time, the blocks were sectioned to obtain sticks with cross-sectional area of 1.0mm2. The specimens were loaded to failure in a universal testing machine at a crosshead speed of 0.5mm/min. The fractured surface morphology of the debonded specimens was observed (40X) to evaluate the fracture pattern. Failure modes were classified as adhesive, cohesive in ceramic, cohesive in resin cement and mixed. The ceramic treatment and the aging method significantly affected the microtensile bond strength. Nd:YAG surface treatment resulted in the best bond strength values. To groups luted with Panavia F cement the microtensile bond strength values were: SW: 27,71±6,3; RW: 35,67±5,13; NdW: 42,49±6,8; NdRW: 37,41±4,76; SH: 22,27±6,05; RH: 27,49±8,83; NdH: 32,24±6,94; NdRH: 31,75±7,77. To groups luted with RelyX cement: SW: 26,74±6,34; RW: 35,07±6,02; NdW: 41,05±7,71; NdRW: 33,85±6,03; SH: 22,77±7,37; RH: 27,84±6,26; NdH: 36,42±5,08; NdRH: 27,6±5,8. Nd:YAG laser was the most effective surface treatment, followed by Nd:YAG+Rocatec, Rocatec and Al2O3 sandblasting. Resin cements presented similar behaviors in spite of aging. NaOCl 12h-immersion decreased Bond strength values.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-03-16
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.