• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Tesis Doctoral
DOI
10.11606/T.23.2005.tde-06062005-155036
Documento
Autor
Nombre completo
Mauricio José Arrais
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2005
Director
Tribunal
Yamada, Roberto Nobuaki (Presidente)
Costa, Bruno
Dias, Reinaldo Brito e
Mathias, Alênio Calil
Sesma, Newton
Título en portugués
Estudo in vitro da deformação permanente em grampos a barra fundidos em ligas de cobalto-cromo e em titânio comercialmente puro, submetidos a testes de tensão-deformação.
Palabras clave en portugués
Grampos dentários
Prótese parcial removível
Resumen en portugués
Foram realizados testes de inserção e remoção de grampos a barra em “I”, fundidos com liga de Cobalto-Cromo (CoCr) e com Titânio comercialmente puro (Ti). Foi utilizada uma máquina oscilante de teste para verificar o comportamento elástico destes grampos que atuaram sobre superfícies metálicas com graus de retenção de 0,25mm e 0,50mm. Dez grampos de CoCr e dez de Ti foram submetidos a 12.500 ciclos de teste (cada) sobre as superfícies metálicas. A ocorrência da deformação permanente dos grampos foi mensurada por meio de relógios comparadores colocados sobre as pontas dos retentores, sendo que a leitura destes relógios ocorreu a cada 500 ciclos. Os resultados desta pesquisa in vitro indicaram que, após os 12.500 ciclos, não foram observadas fraturas nos grampos. E ainda que os grampos feitos em liga de CoCr sofreram menores deformações permanentes do que os de Ti para ambas as retenções.
Título en inglés
Permanent deformation in vitro study of “I” bar clasps cast with cobalt-chromium alloy and commercially pure Titanium, submitted to tension-deformation trials.
Palabras clave en inglés
Dental clasps
Denture partial removable
Resumen en inglés
Insertion and removal trials of “I” bar clasps cast with cobalt-chromium alloy and commercially pure Titanium were carried out. An oscillating trial machine was utilized to verify the elastic behavior of these clasps, which acted on metallic surfaces with 0.25mm and 0.50mm degrees of retention. Ten CoCr clasps and ten Ti clasps were submitted to 12,500 trial cycles (each) on the metallic surfaces. The permanent deformation of the clasps was measured b y comparative gauges placed on the tips of the clasps, and the reading of the gauges was carried out every 500 cycles. The results of this in vitro research showed that after the 12,500 cycles clasp fractures were not observed and that clasps made with CoCr alloy suffered less permanent deformation than Ti ones for both degrees of retention.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
TESEToda.pdf (876.94 Kbytes)
Fecha de Publicación
2005-06-23
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.