Thèse de Doctorat
DOI
10.11606/T.23.2005.tde-06062005-155036
Document
Auteur
Nom complet
Mauricio José Arrais
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2005
Directeur
Jury
Yamada, Roberto Nobuaki (Président)
Costa, Bruno
Dias, Reinaldo Brito e
Mathias, Alênio Calil
Sesma, Newton
Titre en portugais
Estudo in vitro da deformação permanente em grampos a barra fundidos em ligas de cobalto-cromo e em titânio comercialmente puro, submetidos a testes de tensão-deformação.
Mots-clés en portugais
Grampos dentários
Prótese parcial removível
Resumé en portugais
Foram realizados testes de inserção e remoção de grampos a barra em “I”, fundidos com liga de Cobalto-Cromo (CoCr) e com Titânio comercialmente puro (Ti). Foi utilizada uma máquina oscilante de teste para verificar o comportamento elástico destes grampos que atuaram sobre superfícies metálicas com graus de retenção de 0,25mm e 0,50mm. Dez grampos de CoCr e dez de Ti foram submetidos a 12.500 ciclos de teste (cada) sobre as superfícies metálicas. A ocorrência da deformação permanente dos grampos foi mensurada por meio de relógios comparadores colocados sobre as pontas dos retentores, sendo que a leitura destes relógios ocorreu a cada 500 ciclos. Os resultados desta pesquisa in vitro indicaram que, após os 12.500 ciclos, não foram observadas fraturas nos grampos. E ainda que os grampos feitos em liga de CoCr sofreram menores deformações permanentes do que os de Ti para ambas as retenções.
Titre en anglais
Permanent deformation in vitro study of “I” bar clasps cast with cobalt-chromium alloy and commercially pure Titanium, submitted to tension-deformation trials.
Mots-clés en anglais
Dental clasps
Denture partial removable
Resumé en anglais
Insertion and removal trials of “I” bar clasps cast with cobalt-chromium alloy and commercially pure Titanium were carried out. An oscillating trial machine was utilized to verify the elastic behavior of these clasps, which acted on metallic surfaces with 0.25mm and 0.50mm degrees of retention. Ten CoCr clasps and ten Ti clasps were submitted to 12,500 trial cycles (each) on the metallic surfaces. The permanent deformation of the clasps was measured b y comparative gauges placed on the tips of the clasps, and the reading of the gauges was carried out every 500 cycles. The results of this in vitro research showed that after the 12,500 cycles clasp fractures were not observed and that clasps made with CoCr alloy suffered less permanent deformation than Ti ones for both degrees of retention.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
TESEToda.pdf (876.94 Kbytes)
Date de Publication
2005-06-23
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.