Disertación de Maestría
DOI
10.11606/D.23.2005.tde-12112005-121259
Documento
Autor
Nombre completo
Emerson Nakao
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2005
Director
Tribunal
Campos, Tomie Nakakuki de (Presidente)
Adachi, Lena Katekawa
Penna, Luiz Alberto Placido
Título en portugués
"Avaliação da retenção de coroas metálicas fundidas em função dos tipos de agentes cimentantes e das ciclagens térmica e mecânica"
Palabras clave en portugués
Ciclagem mecânica
Ciclagem térmica
Cimentos
Coroas metálicas fundidas
Prótese dentária
Retenção
Resumen en portugués
Nesta pesquisa, foram avaliados a retenção de coroas cimentadas sobre dentes terceiros molares humanos extraídos, após submetê-los às ciclagens térmica e mecânica, e o tipo de falha dos cimentos. Vinte dentes foram preparados de maneira padronizada, com 4 mm de altura, 8 mm de diâmetro e 20º de expulsividade. Coroas metálicas fundidas em NiCr foram cimentadas sobre os preparos, sendo dez com cimento de fosfato de zinco e dez com cimento resinoso, e armazenadas em água a 37ºC por 24 horas. Aleatoriamente, a metade das amostras de ambos os cimentos foi submetida a termociclagem (5ºC e 55ºC ±1ºC por 700 ciclos), seguida de ensaios mecânicos (freqüência de 2 Hz, carga compressiva de 141N por 200.000 ciclos). A outra metade das amostras (grupo controle) não foi submetida aos testes de fadiga. Realizou-se o teste de tração e os valores obtidos foram tratados estatisticamente pelo teste ANOVA (Tukey-Kramer Multiple Comparisons Test). Os resultados mostraram retenção significativamente superior do cimento resinoso Panavia F (valor médio 569,43 N) sobre o cimento de fosfato de zinco (valor médio 350 N). Os testes de envelhecimentos mostraram-se significantes (p<0,001) na sua influência sobre a retenção das coroas, exceto para o grupo cimentado com fosfato de zinco (p>0,05). A falha do cimento observada foi de natureza adesiva para todos os grupos.
Título en inglés
Evaluation of cast crowns’ retention with two different lutting agents after thermocycling and mechanical load
Palabras clave en inglés
Cast crowns
Cements
Dental prostheses
Mechanical load
Retention strength
Thermal stress
Resumen en inglés
The aim of this study was to evaluate the retention of NiCr cast metal crowns fixed with two different lutting agents after thermocycling and mechanical load. The nature of the cement failure was evaluated too. Twenty natural human molar teeth extracted were selected (Banco de Dentes Permanentes Humanos da Faculdade de Odontologia da Universidade de São Paulo – SP). They were prepared at 4mm height, 8mm diameter and 20º of convergence. The cast crowns were lutted with zinc phosphate cement (n=10) and resin cement (n=10) and stored in water at 37ºC for 24 hours. Randomly the half of the specimens of each cement were thermal (5ºC and 55ºC for 700 cycles) and load cycled (2 Hz, 141 N load for 200.000 cycles). The control group did not perform the thermal or fatigue tests. The pull-out test was performed and the results showed a significant (confidence interval 95%) superior retentive strength for Panavia F resin cement (mean value 569,43 N) when compared with zinc phosphate (mean value 350 N). The aging tests were significant (p<0,001) about their influence over the retention of the crowns. They was no significant difference between control and cycled group for crowns lutted with phosphate cement (p>0,05). Adhesive failure of the cements was observed for all subjects.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EmersonNakao.pdf (589.62 Kbytes)
Fecha de Publicación
2006-01-16
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.