Tesis Doctoral
DOI
10.11606/T.23.2005.tde-14102005-122104
Documento
Autor
Nombre completo
Tarcisio José de Arruda Paes Junior
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2005
Director
Tribunal
Kiausinis, Vyto (Presidente)
Kimpara, Estevao Tomomitsu
Luchini, Luiz Carlos
Netto, Henrique Cerveira
Yamada, Roberto Nobuaki
Título en portugués
"Estudo das resinas acrílicas para bases de próteses totais com relação à resistência flexural, e à quantidade de monômero residual superficial"
Palabras clave en portugués
monômero residual
prótese total
resina acrílica
resistência flexural
Resumen en portugués
O objetivo deste trabalho foi o de avaliar a resistência à flexão e a quantidade de monômero residual superficial em resinas acrílicas para bases de próteses totais. Para tanto foram confeccionados corpos-de-prova nas dimensões de 2.5mm x 10mm x 65mm, utilizados em ambas as análises. Padronizou-se o processo de inclusão no qual foram empregadas muflas plásticas reforçadas por fibras de vidro. Sete grupos foram constituídos, de acordo com o tipo de processamento empregado na polimerização das resinas: Ac (Acron-MC) e Vw (Vipi-Wave) de ativação por energia de microondas; Lt (Lucitone 550 – grupo controle) e Vc (Vipi-Cril), resinas de ativação térmica convencional em banho de água aquecida no ciclo longo; Qc (QC-20), uma resina de ativação térmica em ciclo rápido e, dois grupos cuja resina era a mesma de ativação química (Vipi-Flash), processada em duas condições – à temperatura ambiente (Vf1) e, por aquecimento adicional em banho de água (Vf2). Os resultados mostraram diferenças estatisticamente significantes, onde o grupo Ac obteve as maiores médias para resistência flexural e os menores níveis de monômero liberado em relação às demais resinas. Os grupos Qc e Vf1 evidenciaram os piores resultados para ambos os testes, e a princípio, pareceu haver uma relação de causa e efeito entre, os elevados níveis de monômero residual encontrado nestes grupos, e a baixa resistência flexural observada. Verificou-se ainda que a imersão em água aquecida por 30min, da resina de ativação química, propiciou um ganho em qualidade do material para as características avaliadas.
Título en inglés
Study of acrylic resin for complete denture considering flexural strength and quantity of superficial residual mono mer
Palabras clave en inglés
acrylic resin
complete denture
flexural strenght
residual monomer
Resumen en inglés
The purpose of this work was the evaluation of flexural strength and quantity of superficial residual monomer in acrylic resin for complete denture. To perform both analyses it was developed specimens with a dimension of 2.5mm x 10mm x 65mm. The inclusion process was standardized by the use of plastic flasks reinforced with fiberglass. Seven groups were constituted in accordance with the type of resin polymerization process: Ac (Acron-MC) and Vw (Vipi-Wave) activated by microwave energy; Lt (Lucitone 550 – control group) and Vc (Vipi-Cril), conventional water bath curing cycles of heat activated acrylic resin; Qc (QC-20), fast cycle thermal activation; and two groups of self cured resin (Vipi-Flash), processed in two distinguished conditions: ambient temperature (Vf1) and additional heating in water bath (Vf2). The results have shown statistical significant differences. The Ac group had the highest mean to flexural resistance and the least level of released monomer in comparison with others resins. The Qc and Vf1 groups had the worst results for both tests. The initial conclusions showed a cause-effect relation between higher levels of residual monomer and lower flexural strength to this group. Additionally, it was verified that the immersion for 30 minutes of self cured resin in heated water gave an improvement of material quality to evaluated characteristics.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
TarcisioTeseToda.pdf (1.13 Mbytes)
Fecha de Publicación
2005-10-27
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.