Thèse de Doctorat
DOI
10.11606/T.23.2005.tde-14102005-122104
Document
Auteur
Nom complet
Tarcisio José de Arruda Paes Junior
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2005
Directeur
Jury
Kiausinis, Vyto (Président)
Kimpara, Estevao Tomomitsu
Luchini, Luiz Carlos
Netto, Henrique Cerveira
Yamada, Roberto Nobuaki
Titre en portugais
"Estudo das resinas acrílicas para bases de próteses totais com relação à resistência flexural, e à quantidade de monômero residual superficial"
Mots-clés en portugais
monômero residual
prótese total
resina acrílica
resistência flexural
Resumé en portugais
O objetivo deste trabalho foi o de avaliar a resistência à flexão e a quantidade de monômero residual superficial em resinas acrílicas para bases de próteses totais. Para tanto foram confeccionados corpos-de-prova nas dimensões de 2.5mm x 10mm x 65mm, utilizados em ambas as análises. Padronizou-se o processo de inclusão no qual foram empregadas muflas plásticas reforçadas por fibras de vidro. Sete grupos foram constituídos, de acordo com o tipo de processamento empregado na polimerização das resinas: Ac (Acron-MC) e Vw (Vipi-Wave) de ativação por energia de microondas; Lt (Lucitone 550 – grupo controle) e Vc (Vipi-Cril), resinas de ativação térmica convencional em banho de água aquecida no ciclo longo; Qc (QC-20), uma resina de ativação térmica em ciclo rápido e, dois grupos cuja resina era a mesma de ativação química (Vipi-Flash), processada em duas condições – à temperatura ambiente (Vf1) e, por aquecimento adicional em banho de água (Vf2). Os resultados mostraram diferenças estatisticamente significantes, onde o grupo Ac obteve as maiores médias para resistência flexural e os menores níveis de monômero liberado em relação às demais resinas. Os grupos Qc e Vf1 evidenciaram os piores resultados para ambos os testes, e a princípio, pareceu haver uma relação de causa e efeito entre, os elevados níveis de monômero residual encontrado nestes grupos, e a baixa resistência flexural observada. Verificou-se ainda que a imersão em água aquecida por 30min, da resina de ativação química, propiciou um ganho em qualidade do material para as características avaliadas.
Titre en anglais
Study of acrylic resin for complete denture considering flexural strength and quantity of superficial residual mono mer
Mots-clés en anglais
acrylic resin
complete denture
flexural strenght
residual monomer
Resumé en anglais
The purpose of this work was the evaluation of flexural strength and quantity of superficial residual monomer in acrylic resin for complete denture. To perform both analyses it was developed specimens with a dimension of 2.5mm x 10mm x 65mm. The inclusion process was standardized by the use of plastic flasks reinforced with fiberglass. Seven groups were constituted in accordance with the type of resin polymerization process: Ac (Acron-MC) and Vw (Vipi-Wave) activated by microwave energy; Lt (Lucitone 550 – control group) and Vc (Vipi-Cril), conventional water bath curing cycles of heat activated acrylic resin; Qc (QC-20), fast cycle thermal activation; and two groups of self cured resin (Vipi-Flash), processed in two distinguished conditions: ambient temperature (Vf1) and additional heating in water bath (Vf2). The results have shown statistical significant differences. The Ac group had the highest mean to flexural resistance and the least level of released monomer in comparison with others resins. The Qc and Vf1 groups had the worst results for both tests. The initial conclusions showed a cause-effect relation between higher levels of residual monomer and lower flexural strength to this group. Additionally, it was verified that the immersion for 30 minutes of self cured resin in heated water gave an improvement of material quality to evaluated characteristics.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
TarcisioTeseToda.pdf (1.13 Mbytes)
Date de Publication
2005-10-27
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.