Thèse de Doctorat
DOI
10.11606/T.23.2007.tde-02012008-153128
Document
Auteur
Nom complet
José Roberto de Oliveira Bauer
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2007
Directeur
Jury
Rodrigues Filho, Leonardo Eloy (Président)
Adabo, Gelson Luiz
Bezzon, Osvaldo Luiz
Henriques, Guilherme Elias Pessanha
Muench, Antonio
Titre en portugais
Propriedades mecânicas do titânio comercialmente puro e da liga Ti-6Al-4V fundidos em diferentes ambientes
Mots-clés en portugais
Argônio
Propriedades mecânicas
Resistência à tração
Técnica de fundição Odontológica
Teste de dureza
Titânio
Resumé en portugais
Problema: O emprego do titânio e ligas de titânio para aplicações médicas e odontológicas tem aumentado nas últimas décadas, porém, o alto custo do material desestimula o seu uso rotineiro. Objetivos: Avaliar o efeito da pureza do argônio nas propriedades mecânicas, microestrutura e modo de fratura do titânio comercialmente puro (Grau I) e da liga Ti-6Al-4V. Material e Métodos: As fundições para cada liga foram realizadas em uma máquina de indução eletromagnética com um argônio de alta pureza (99,999%) e um argônio conhecido como industrial (99,98%). Os testes de resistência à tração, limite de proporcionalidade e alongamento foram realizados em máquina de ensaio universal sob velocidade de 1 mm/min. Os espécimes fraturados foram embutidos em resina fenólica (baquelite) e polidas para a realização da microdureza Vickers (100g/15s), a a 25, 50, 100, 200 e 500?m da borda do corpo-de-prova. A microestrutura das ligas também foi analisada em alguns espécimes, com o objetivo de avaliar a superfície fraturada dos espécimes alguns foram submetidos à microscopia eletrônica de varredura. Análise estatística: Os dados provenientes de cada teste mecânico foram submetidos a uma análise de variância (tipo de titânio vs. pureza do argônio) e teste de Tukey (? = 0,05). Os dados de microdureza Vickers foram submetidos a uma análise de variância de medidas repetidas (fatores principais: liga e argônio) e medida repetida: distância e teste de Tukey para o contraste entre médias (? = 0,05). Resultados: O grau de pureza do gás não influenciou os valores do limite de proporcionalidade, da resistência à tração e alongamento, assim como a microdureza Vickers, microestrutura e padrão de fratura. A liga Ti-6Al-4V apresentou alto valores de resistência à tração, limite de proporcionalidade e microdureza Vickers, e baixo alongamento. A microdureza dos materiais foi alta nas proximidades da borda, mas a pureza do argônio não teve influência alguma. Conclusões: O argônio industrial pode ser utilizado para realizar as fundições do Ti CP e Ti-6Al-4V sem prejuízos nas suas propriedades.
Titre en anglais
Mechanical properties of commercially pure titanium and Ti-6Al-4V alloys casting in different environments
Mots-clés en anglais
Argon
Dental casting technique
Hardness test
Mechanical properties
Tensile strength
Titanium
Resumé en anglais
Background: Although CP titanium and titanium alloys have been used for medical and dental applications, their high cost has not stimulated their current use. Objective: The purpose of this study was to evaluate the effect of argon purity on the mechanical properties, microstructure and fractography of CP Ti (Grade I) and Ti-6Al- 4V cast alloys. Material and Methods: The castings for each alloy were made in a centrifugal casting machine using either a high-purity (99.999%) and or an industrial argon gas (99.98%). The ultimate tensile strength (UTS), proportional limit (PL) and elongation (EL) were evaluated in a universal testing machine at a crosshead speed of 1 mm/min. The fractured specimens were embedded in phenolic resin and polished down for Vicker's microhardness (VHN) measurement (100g, 15s) from 25 ?m below the cast surface, then at 50?m, 100?m, 200?m and 500?m. The microstructures of the alloys were also revealed. Scanning electron microscopy fractography was undertaken for the fractured surfaces after tensile testing. The data from the mechanical tests and hardness were subjected to a two-way ANOVA and Tukey's test (? = 0.05). Results: The mean values of UTS, PL, EL and VHN were not affected by the argon gas purity. Higher UTS, PL and VHN and lower EL was observed for Ti-6Al-4V. The microhardness values of both alloys were higher at the surface layers and it was not influenced by the argon gas purity. Conclusions: It was concluded that the industrial argon gas can be safely used to cast CP Ti and Ti-6Al- 4V, since it does not alter the mechanical properties of the studied alloys.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Bauer.pdf (11.73 Mbytes)
Date de Publication
2008-06-09
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.