Tesis Doctoral
DOI
Documento
Autor
Nombre completo
Marcelo Geovanny Cascante Calderon
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2018
Director
Tribunal
Medeiros, Igor Studart (Presidente)
Rodrigues Filho, Leonardo Eloy
Sgura, Ricardo
Silva, Lucas Hian da
Título en portugués
Influência do aquecimento de agentes de acoplamento químico na resistência de união de um cimento resinoso à zircônia
Palabras clave en portugués
Acoplamento químico
Adesivo universal
Aquecimento
Primer cerâmico
Resistência de união
Zirconia
Resumen en portugués
Esta pesquisa in vitro avaliou a influência do aquecimento de diferentes agentes de acoplamento na resistência de união de um cimento resinoso (Panavia F2.0®/Kuraray Noritake. Japão) e uma zircônia (Y-TZP - YZ ). Inicialmente, placas de zircônia foram silicatizadas com o sistema Rocatec (3M / ESPE). Foram aplicados os agentes de acoplamento químico: Single Bond Universal (3M/ESPE); Monobond N (Ivoclar Vivadent) e Clearfil Ceramic Primer (Kuraray Co); após, foram aquecidos em um forno resistivo em diferentes temperaturas (750C e 1000C) por 5 min, antes da cimentação resinosa de um cilindro de resina composta previamente confeccionado (diam. 0,8 mm). Os grupos controle de cada agente de acoplamento foram mantidos à temperatura ambiente (240C). Metade dos corpos-de-prova foi submetida imediatamente ao teste de microcisalhamento (0,5 mm/min) realizado com auxílio de um fio ortodôntico e a outra metade envelhecida por meio de a 2.000 ciclos térmicos (50C e 550C), seguido de armazenamento em água destilada a 370 C por 2 meses, antes do ensaio mecânico. A análise de variância de três fatores (ANOVA) e o teste de Tukey (p?0,05) mostraram que o aquecimento dos agentes químicos de acoplamento produziu maiores valores de resistência de união entre o cimento e a zircônia. A resistência de união imediata foi superior para o Monobond N (30 MPa) e Single Bond Universal (32,5 MPa). Após o envelhecimento, houve redução da resistência de união em todos os grupos e o grupo Monobond N (16,9 MPa) apresentou resistência de união superior à dos demais. A associação de um tratamento térmico simples a um agente de acoplamento é válida para produzir resistência de união superior entre o cimento resinoso e a zircônia.
Título en inglés
Influence of heating of chemical coupling agents on the bond strength of a resin cement to zirconia
Palabras clave en inglés
Bonding strength
Chemical coupling agents
Heating
Primer ceramic
Universal adhesive
Zirconia
Resumen en inglés
This in vitro study evaluated the influence of the heating different coupling agents on microshear bond strength between zirconia (Y-TZP-YZ ) and a resin cement (Panavia F2.0® / Kuraray Noritake, Japan). Initially, the zirconia blocks were silicoated with the Rocatec system (3M / ESPE). After, the chemical coupling agents were applied: Single Bond Universal (3M / ESPE); Monobond N (Ivoclar Vivadent) and Clearfil Ceramic Primer (Kuraray Co). They were then heated in a resistive furnace at different temperatures (750C and 1000C) for 5 min prior to resin cementation of a preformed resin composite cilinder (0.8 mm diameter). Control groups were maintained at room temperature (240C). Half of the specimens were immediately submitted to the microshear test (0.5 mm/min) performed with an orthodontic wire and the other half was subjected to 2,000 thermal cycles (50C and 550C), followed by storage in distilled water at 370C for 2 months before the microshear test. 3-way ANOVA and Tukey's test (p<0.05) showed that the heating of the chemical coupling agents produced higher bond strength between the ceramic and resin cement. Immediate bond strength was superior for Monobond N (30 MPa) and Single Bond Universal (32,5 MPa). After aging, there was reduction of bond strength in all groups and the Monobond N group (16,9 MPa) was superior to the others. The combination of a simple heat treatment with a coupling agent is valid to produce greater bond strength.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2019-06-27
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.