Thèse de Doctorat
DOI
Document
Auteur
Nom complet
Marcelo Geovanny Cascante Calderon
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2018
Directeur
Jury
Medeiros, Igor Studart (Président)
Rodrigues Filho, Leonardo Eloy
Sgura, Ricardo
Silva, Lucas Hian da
Titre en portugais
Influência do aquecimento de agentes de acoplamento químico na resistência de união de um cimento resinoso à zircônia
Mots-clés en portugais
Acoplamento químico
Adesivo universal
Aquecimento
Primer cerâmico
Resistência de união
Zirconia
Resumé en portugais
Esta pesquisa in vitro avaliou a influência do aquecimento de diferentes agentes de acoplamento na resistência de união de um cimento resinoso (Panavia F2.0®/Kuraray Noritake. Japão) e uma zircônia (Y-TZP - YZ ). Inicialmente, placas de zircônia foram silicatizadas com o sistema Rocatec (3M / ESPE). Foram aplicados os agentes de acoplamento químico: Single Bond Universal (3M/ESPE); Monobond N (Ivoclar Vivadent) e Clearfil Ceramic Primer (Kuraray Co); após, foram aquecidos em um forno resistivo em diferentes temperaturas (750C e 1000C) por 5 min, antes da cimentação resinosa de um cilindro de resina composta previamente confeccionado (diam. 0,8 mm). Os grupos controle de cada agente de acoplamento foram mantidos à temperatura ambiente (240C). Metade dos corpos-de-prova foi submetida imediatamente ao teste de microcisalhamento (0,5 mm/min) realizado com auxílio de um fio ortodôntico e a outra metade envelhecida por meio de a 2.000 ciclos térmicos (50C e 550C), seguido de armazenamento em água destilada a 370 C por 2 meses, antes do ensaio mecânico. A análise de variância de três fatores (ANOVA) e o teste de Tukey (p?0,05) mostraram que o aquecimento dos agentes químicos de acoplamento produziu maiores valores de resistência de união entre o cimento e a zircônia. A resistência de união imediata foi superior para o Monobond N (30 MPa) e Single Bond Universal (32,5 MPa). Após o envelhecimento, houve redução da resistência de união em todos os grupos e o grupo Monobond N (16,9 MPa) apresentou resistência de união superior à dos demais. A associação de um tratamento térmico simples a um agente de acoplamento é válida para produzir resistência de união superior entre o cimento resinoso e a zircônia.
Titre en anglais
Influence of heating of chemical coupling agents on the bond strength of a resin cement to zirconia
Mots-clés en anglais
Bonding strength
Chemical coupling agents
Heating
Primer ceramic
Universal adhesive
Zirconia
Resumé en anglais
This in vitro study evaluated the influence of the heating different coupling agents on microshear bond strength between zirconia (Y-TZP-YZ ) and a resin cement (Panavia F2.0® / Kuraray Noritake, Japan). Initially, the zirconia blocks were silicoated with the Rocatec system (3M / ESPE). After, the chemical coupling agents were applied: Single Bond Universal (3M / ESPE); Monobond N (Ivoclar Vivadent) and Clearfil Ceramic Primer (Kuraray Co). They were then heated in a resistive furnace at different temperatures (750C and 1000C) for 5 min prior to resin cementation of a preformed resin composite cilinder (0.8 mm diameter). Control groups were maintained at room temperature (240C). Half of the specimens were immediately submitted to the microshear test (0.5 mm/min) performed with an orthodontic wire and the other half was subjected to 2,000 thermal cycles (50C and 550C), followed by storage in distilled water at 370C for 2 months before the microshear test. 3-way ANOVA and Tukey's test (p<0.05) showed that the heating of the chemical coupling agents produced higher bond strength between the ceramic and resin cement. Immediate bond strength was superior for Monobond N (30 MPa) and Single Bond Universal (32,5 MPa). After aging, there was reduction of bond strength in all groups and the Monobond N group (16,9 MPa) was superior to the others. The combination of a simple heat treatment with a coupling agent is valid to produce greater bond strength.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2019-06-27
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.