Thèse de Doctorat
DOI
10.11606/T.23.2005.tde-11012006-124342
Document
Auteur
Nom complet
Ana Maria Lima Almeida
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2005
Directeur
Jury
Francci, Carlos Eduardo (Président)
Adabo, Gelson Luiz
Alves, Claudia Maria Coêlho
Cesar, Paulo Francisco
Geraldeli, Saulo
Titre en portugais
"Diferentes métodos de otimização da polimerização de resinas compostas de uso direto"
Mots-clés en portugais
tratamento pós-cura
autoclave
forno
microdureza Knoop
polimerização
resina composta
resistência à flexão
Resumé en portugais
Este trabalho avaliou a influência da densidade de energia da pré-cura, e de diferentes tratamentos pós-cura na otimização das propriedades físicas (Resistência à Flexão e Dureza Knoop) de resinas compostas diretas, visando a possibilidade de indicação para restauraçoes indiretas. Foram usadas as resinas diretas Fillmagic, Concept, Glacier, Z100, Masterfill e W3D Master e as indiretas Solidex e Belleglass HP como controle. Para cada resina direta foram confeccionados 60 espécimes em barra (10x2x2mm), 30 irradiados em uma face e 30 nas duas faces (30 espécimes = 10 controle, 10 autoclave e 10 forno de luz). Para as resinas indiretas foram preparados 10 espécimes conforme processamento de seus fabricantes. 380 espécimes foram submetidos ao ensaio de resistência à flexão (Kratos). De cada condição experimental, 10 fragmentos foram usados para ensaio de microdureza Knoop (Shimadzu HMV-2). A análise de variância e o teste de Tukey demonstraram significância para resistência à flexão nos fatores Resina (p<0,001) e Tratamento (p=0,001) e na interação Resina x Tratamento (p=0,001). Para a microdureza Knoop os três fatores e as interações foram significantes: Resina (p=0,001); Face (p=0,001) Tratamento (p=0,017); Resina x Face (p=0,001); Resina x Tratamento (p=0,007); Face x Tratamento (p=0,001) e Resina x Face x Tratamento (p=0,024). A maior média de cada resina direta, independente da condição experimental, foi comparada às médias das resinas indiretas. Os resultados apontam que na resistência à flexão (Z100 = W3D = Fillmagic = Glacier) e (Z100 > Masterfill > Belleglass HP > Concept > Solidex). Na Dureza Knoop (Z100 > Belleglass HP, Fillmagic, W3D, Concept, Glacier, Masterfill e Solidex). Conclusão: as propriedades físicas (resistência à flexão e dureza Knoop) não são obstáculos na indicação de resinas compostas de uso direto para restaurações indiretas
Titre en anglais
Different methods in optimizing the polymerization of direct resin composites
Mots-clés en anglais
autoclave
composite resin
flexural strength
Knoop microhardness
oven
polymerization
post-cure treatment
Resumé en anglais
This study evaluated the influence of pre-cure energy density, and additional post-cure treatments in optimizing the physical properties (Flexural strength and Knoop microhardness) of direct resin composites with the aim at allowing their use for indirect restorations. Direct resin composites evaluated were Fillmagic, Concept, Glacier, Z100, Masterfill and W3D Master; indirect composites were Solidex and Belleglass HP. Sixty bar-shaped specimens (10x2x2mm) were prepared for each material, so that 30 of them were light-cured by one surface and 30 on both surfaces. From the 30 specimens of each group, 10 were control, 10 were submitted to additional autoclave and 10 to light oven treatment. Ten specimens were prepared with each indirect composite following the manufactures’ recommendations. The 380 specimens were submitted to flexural strength test (Kratos universal testing machine), and values obtained at fracture were reported. After that, 10 fragments were chosen for each experimental condition and assessed for Knoop microhardness (Shimadzu HMV-2). Data were submitted to analysis of variance and Tukey’s test at p<0.05. Statistically significant differences were found among flexural strength results regarding composite materials (p<0.001), treatments (p<0.001) and interactions (composite x treatment, p<0.001). Regarding Knoop microhardness, both three factors and their interactions were also significant: composite (p<0.001), surface (p<0.001) and treatment (p<0.017), composite x surface (p<0.001), composite treatment (p<0.001), surface x treatment (p<0.001) and composite x surface x treatment (p<0.024). The highest mean value for each direct composite, regardless of the experimental condition, was compared to the mean values obtained for the indirect materials. With regard to flexural strength, comparisons point out that Z100 = W3D = Fillmagic = Glacier and Z100 > Masterfill > Belleglass HP > Concept > Solidex, whereas for Knoop microhardness Z100 > Belleglass HP, Fillmagic, W3D, Concept, Glacier, Masterfill and Solidex. Conclusion: considering the physical properties evaluated in this study, they are not an obstacle to the indication of direct composites for indirect restorations
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
AnaMariaLAlmeida.pdf (2.08 Mbytes)
Date de Publication
2006-04-03
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.