Thèse de Doctorat
DOI
10.11606/T.23.2005.tde-12012006-155419
Document
Auteur
Nom complet
Ivone Lima Santana
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2005
Directeur
Jury
Rodrigues Filho, Leonardo Eloy (Président)
Alves, Claudia Maria Coêlho
Matos, Jivaldo do Rosario
Rodrigues, Celia Regina Martins Delgado
Silva, Alessandra Reis
Titre en portugais
"Estudo da influência do tratamento por calor em propriedades mecânicas de resinas compostas"
Mots-clés en portugais
Dureza
Resina composta
Resistência à flexão
Tratamento térmico adicional
Resumé en portugais
O objetivo deste trabalho foi o de avaliar o efeito de tratamentos por calor nas propriedades mecânicas de resistência flexional e microdureza Knoop de três marcas comerciais de resinas compostas para uso direto (FillMagic, P60 e TPH), na condição de incluída ou não em revestimento durante um tratamento térmico (calor seco/170°C), por três períodos (5, 10 e 15 min). A temperatura adotada para os tratamentos foi baseada em análises prévias (termogravimetria e calorimetria exploratória diferencial) com a finalidade de se determinar a temperatura de início de perda de massa e de transição vítrea das resinas. Os corpos-de-prova (n=7) foram confeccionados com o auxílio de uma matriz metálica (10 mm x 2 mm x 2 mm), sendo o compósito inserido em bloco único e irradiado numa única superfície (600mW/cm 2 por 40s). Foram obtidos, no total, sete grupos experimentais por resina, sendo o controle a condição de apenas fotoativada. Os espécimes foram submetidos ao ensaio de resistência à flexão, com distância entre apoios de 8 mm, em uma velocidade constante de 0,5 mm/min e célula de carga de 1000N. A dureza Knoop foi obtida com carga de 100 g e tempo de penetração de 15 s. As médias de resistência flexional, em MPa, foram de 174,80 para a resina FillMagic, 182,64 para a P60 e 172,22 para a TPH. Na mesma ordem, as médias de microdureza Knoop foram de 73,1; 102,0 e 74,0.A análise de variância dos resultados obtidos permitiram concluir que os tratamentos experimentais aumentaram a resistência flexional das resinas indistintamente. Os valores de microdureza também aumentaram, mas houveram diferenças de suscetibilidade ao tratamento térmico entre as resinas
Titre en anglais
Influence of heat treatment on the mechanical properties of resin composites
Mots-clés en anglais
Additional heat-treated
Flexural strength
Hardness
Resin composite
Resumé en anglais
The aim of this study was to assess the effect of heat treatment on mechanical properties of flexure strength and Knoop micro hardness of three commercially available brands of resin composites for direct use (FillMagic, P60 and TPH) included or not in investments during heat treatment (dry heat/170ºC) by three periods (5, 10 and 15 min.) The temperature adopted for the treatments was based on previous analysis (thermo gravimetric and differential exploratory heating) in order to determine the initial temperature of mass loss and glass transition of resin composites. The samples (n=7) were prepared with a metallic matrix (10 mm x 2mm x 2mm) in which the resin composite was inserted in a single block and only one surface was irradiated (600mW/cm 2 40s). Seven experimental groups were obtained for each resin composite in which the control group was solely light-cured. The flexure strength test was performed with a support distance of 8 mm, cross-head speed of 0.5 mm/min. and 1000 N load. Knoop micro hardness was obtained with a load of 100 g and penetration time of 15 s. The flexure strength averages in MPa were 174.80 for FillMagic, 182. 64 for P60 and 172. 22 for TPH. Thus, Knoop micro hardness means were 73.1; 102.0 and 74.0. The analysis of variance indicated that the experimental treatments increased flexure strength of resin composites. Micro hardness values also increased, but there were differences in the resin composites susceptibility to the heat treatment
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
IvoneLSantanaTese.pdf (343.47 Kbytes)
Date de Publication
2006-04-03
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.