Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.23.2014.tde-19022015-152739
Document
Auteur
Nom complet
Ranulfo Benedito de Paula Miranda
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2014
Directeur
Jury
Miranda Junior, Walter Gomes (Président)
Marocho, Susana María Salazar
Rigo, Eliana Cristina da Silva
Titre en portugais
Efeito do conteúdo de titânia e da alteração da superfície por meio da aplicação do recobrimento biomimético nas propriedades mecânicas do compósito Y-TZP/TiO2
Mots-clés en portugais
Propriedades mecânicas
Recobrimento biomimético
Titânia
Zircônia
Resumé en portugais
Os objetivos desse trabalho foram: 1) determinar o efeito do conteúdo de titânia em mol % (zero, 10 e 30) na área de superfície específica (SBET), no tamanho dos aglomerados e na intensidade dos picos correspondentes às fases cristalinas presentes no pó cerâmico de Y-TZP/TiO2; 2) determinar o efeito do conteúdo de titânia em mol % (zero, 10 e 30) na microestrutura, densidade, densidade relativa, módulo de elasticidade, coeficiente de Poisson, módulo de Weibull (m) e resistência à flexão (f) de pastilhas cerâmicas sinterizadas de Y-TZP/TiO2 e, 3) determinar o efeito do recobrimento biomimético no módulo de Weibull (m) e na resistência á flexão de pastilhas cerâmicas sinterizadas de Y-TZP/TiO2. Os pós foram produzidos por meio de uma rota de co-precipitação, obtendo-se três composições do compósito Y-TZP/TiO2, que foram de zero (T0), 10 (T10) e 30 (T30) % mol de titânia. O pó produzido foi prensado (50 MPa) para produzir pastilhas de 15 mm de diâmetro e sinterizado a 1400 °C por 2 horas. Após o polimento com solução diamantada de 45 m, as pastilhas (n=60 para cada grupo) ficaram com aproximadamente 12 mm de diâmetro e 1,0 mm de espessura. Metade das pastilhas foram submetidas ao recobrimento biomimético (sete dias em solução de silicato de sódio e sete dias em solução de 1,5 SBF-simulated body fluid). Os pós foram caracterizados por difração de raios-X (DRX), espalhamento a laser, adsorção gasosa e microscopia eletrônica de varredura (MEV). As pastilhas foram caracterizadas pelo método de Archimedes, pulso-eco ultra-ssônico, MEV, DRX e para a análise de Weibull, as pastilhas foram submetidas ao ensaio de resistência à flexão biaxial em saliva artificial a 37°C. Os resultados mostraram que todos os pós apresentaram zircônia monoclínica e tetragonal na sua composição e uma área de superfície específica superior a 42 m2/g. A adição de titânia favoreceu a formação de aglomerados maiores e com uma distribuição bimodal. Em todas as pastilhas foram detectadas zircônia monoclínica e tetragonal, enquanto no grupo T30 também foi detectada a fase de titanato de zircônia (ZrTiO4). O grupo T0 apresentou os maiores valores de densidade medida (6,05 g/cm3), densidade relativa (99,0%), módulo de elasticidade (213 GPa) e resistência à flexão (815 MPa). A adição de titânia reduziu significativamente a densidade medida (5,45 g/cm3 para T10 e 5,15 g/cm3 para T30) a densidade relativa (94,4% para T10 e 96,3% para o T30) o módulo de elasticidade (156 GPa para T10 e 134 GPa para o T30) e a resistência à flexão (455 MPa para o grupo T10 e 336 MPa para o grupo T30) do compósito Y-TZP/TiO2. O grupo T30 apresentou um módulo de Weibull (11,7) e um coeficiente de Poisson (0,34) significativamente superior ao grupo T0 (6,4 e 0,31, respectivamente). Foi observado que o recobrimento biomimético promoveu a formação de glóbulos de hidroxiapatita distribuídos de forma heterogênea na superfície do material e que esse tratamento não alterou significativamente a resistência à flexão e o módulo de Weibull do compósito Y-TZP/TiO2. Conclui-se que a adição de titânia afetou as propriedades estudas do pó e das pastilhas do compósito de Y-TZP/TiO2. Além disso, o compósito pode ser recoberto com uma camada hidroxiapatita sem ter sua confiabilidade estrutural afetada.
Titre en anglais
Effect of titania content and the change of the surface by applying the biomimetic coating on the mechanical properties of the composite Y-TZP/TiO2
Mots-clés en anglais
Biomimetic coating
Mechanical properties
Titania
Zirconia
Resumé en anglais
The objectives of this study were: 1) to determine the effect of titania content in mol% (zero, 10 and 30) in the specific surface area (SBET), the size of the agglomerates and the intensity of the peaks corresponding to crystalline phase present in the ceramic powder of Y-TZP/TiO2; 2) to determine the effect of the content in mol% of titania (zero, 10 and 30) in the microstructure, density, relative density, modulus of elasticity, Poisson's ratio, Weibull modulus (m) and flexural strength (f) of ceramic discs sintered from Y-TZP/TiO2 and 3) to determine the effect of biomimetic coating on the Weibull modulus (m) and the flexural strength of the sintered ceramic discs of Y-TZP/TiO2. The powders were produced by a co-precipitation route, in order to obtain the composite Y-TZP/TiO2 with three compositions, containing zero (T0), 10 (T10) and 30 (T30) mol% titania. The produced powder was pressed (50 MPa) into discs of 15 mm diameter and sintered at 1400 °C for 2 hours. After polishing with diamond solution of 45 m, the discs (n = 60 for each group) were approximately 12 mm in diameter and 1.0 mm-thick. Half of the discs were subjected to biomimetic coating (seven days with sodium silicate solution and seven days in 1,5 SBF-simulated body fluid solution ). The powders were characterized by X-ray diffraction (XRD), laser scattering, gas adsorption and scanning electron microscopy (SEM). The discs were characterized by the Archimedes method, ultrasonic pulse-echo, SEM, XRD and for the Weibull analysis, the discs were subjected to the test of biaxial flexural strength in artificial saliva at 37 °C. The results showed that all powders had monoclinic and tetragonal zirconia in their composition, and a specific surface area greater than 42 m2/g. The titania addition favored the formation of larger agglomerates and a bimodal distribution. In all discs monoclinic and tetragonal zirconia were detected, while in the T30 group zirconium titanate (ZrTiO4) was also detected. T0 group had the highest measured density (6,05 g/cm3), relative density (99,0%), elasticity modulus (213 GPa) and flexural strength (815 MPa). The addition of titania significantly reduced the measured density (5,45 g/cm3 for T10 group and 5,15 g/cm3 for T30 group), the relative density (94,4% for T10 group and 96,3% for T30 group), elasticity modulus (156 GPa for T10 group and 134 GPa for T30 group) and flexural strength (455 MPa for T10 group and 336 MPa for T30 group) of the Y-TZP/TiO2 the composite. The T30 group showed a Weibull modulus (11,7) and Poisson's ratio (0,34) significantly higher than those of T0 group (6,4 and 0,31). It was observed that the biomimetic coating resulted in the formation of apatite globules heterogeneously distributed on the surface of the material and that this treatment did not significantly alter the flexural strength and Weibull modulus of the composite Y-TZP/TiO2. It is concluded that the addition of titania affects the studied properties of the powder and discs of the composite Y-TZP/TiO2. Also, the composite can be coated with a layer of calcium phosphate without affecting its structural reliability.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2015-05-12
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.