Tesis Doctoral
DOI
10.11606/T.23.2013.tde-20022014-192449
Documento
Autor
Nombre completo
Renata Antunes Esteves
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2013
Director
Tribunal
Rodrigues Filho, Leonardo Eloy (Presidente)
Boaro, Letícia Cristina Cidreira
Medeiros, Igor Studart
Silva, Cecy Martins
Turbino, Miriam Lacalle
Título en portugués
Influência da composição da matriz orgânica, conteúdo inorgânico e tratamento térmico sobre diferentes propriedades de compósitos experimentais
Palabras clave en portugués
Grau de conversão
Módulo de elasticidade
Resinas compostas
Resistência à flexão
Tenacidade à fratura
Tratamento térmico
Resumen en portugués
Objetivo: Analisar a influência da matriz orgânica, do conteúdo inorgânico e do tratamento térmico (TT) sobre diferentes propriedades de compósitos experimentais, tais como o grau de conversão (GC), tenacidade à fratura (KIC), resistência à flexão (RF) e módulo de elasticidade (ME). Métodos: Para o experimento foram analisadas seis formulações de compósitos experimentais com proporções molares de Bis-GMA:TEGDMA de 5:5 e 7:3, a carga utilizada foi o vidro de bário, nas concentrações de 30, 50 e 70% em peso, e os fotoiniciadores a amina e canforoquinona. O GC foi analisado através da espectroscopia no infra-vermelho (FTIR) (n=5). A KlC foi avaliada pelo método single-edge notched beam (SENB). As imagens das superfícies de fratura foram capturadas por um estereomicroscópio e a KlC calculada (n=10). A análise da RF e ME foi realizada através do teste dos três pontos (n=10). Para todos os fatores de variação estudados, metade dos espécimes imediatamente após à confecção receberam TT em estufa convencional, a 170º C por 10 minutos e a outra metade não. Após 24 horas, as amostras foram destinadas de acordo com os ensaios realizados. Os dados foram analisados utilizando ANOVA/Tukey para o grau de conversão, tenacidade à fratura e resistência à flexão, e, Kruskal-Wallis para o módulo de elasticidade (=5%). Resultados: Na análise do GC (%) foi observada significância estatística para os três fatores de variação analisados individualmente (monômero, carga e TT), como também, para a interação monômero x TT (p<0,001). Para a KIC e RF, as alterações significantes foram observadas apenas nos três fatores de variação (monômero, carga e TT) analisados individualmente (p<0,001). Para o ME, os fatores individuais (monômero, carga e TT), a interação carga x TT apresentaram significância estatística (p<0,001), bem como a interação monômero x carga (p=0,001). Conclusões: A matriz orgânica e o conteúdo inorgânico dos compósitos experimentais influenciaram o GC, a KIC, a RF e ME, e o TT promoveu melhorias nas propriedades estudadas.
Título en inglés
Influence of composition of the organic matrix, filler content and thermic treatment on different properties of experimental composites
Palabras clave en inglés
Degree of conversion
Elastic modulus
Flexural strength
Fracture toughness
Resin composites
Thermic treatment
Resumen en inglés
Objective: To analyze the influence of organic matrix, the inorganic content and thermic treatment (TT) on different properties of experimental composites, such as the degree of conversion (DC), fracture toughness (KIC), flexural strength (FS) and elastic modulus (EM). Methods: This experiment analyzed six formulations of experimental composites with 5:5 and 7:3 molar proportions of Bis-GMA: TEGDMA. The load used was barium glass at concentrations of 30, 50 and 70% by weight and the photoinitiators, camphorquinone and amine. GC was analyzed by infrared spectroscopy (FTIR) (n=5). The KIC was evaluated by a "single-edge notched beam" (SENB). The images of the fracture surfaces were captured by a stereomicroscope and KIC calculated (n=10). The analysis FS and EM were performed by testing three points (n=10). For all the variation factors studied, half of the specimens immediately after the preparation received TT in conventional oven at 170º C for 10 minutes and the other half not. After 24 hours, the samples were designed according to the tests. Data were analyzed using ANOVA/Tukey the degree of conversion, fracture toughness and flexural strength, and Kruskal-Wallis test for the elastic modulus (=5%). Results: Analysis of GC (%) statistical significance was observed for the three variation factors analyzed individually (monomer, filler and TT), as well as for the interaction monomer x TT (p <0.001). For KIC and FS, significant changes were observed only in the three variation factors (monomer, filler and TT) analyzed individually (p<0.001). For EM, the individual factors (monomer, filler and TT) TT x filler interaction showed statistical significance (p <0.001), as well as the monomer x filler interaction (p = 0.001). Conclusions: The organic matrix and inorganic content of experimental composites influenced the GC, KIC, FS and EM, and the TT caused improvements in the properties studied.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-03-25
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.