Disertación de Maestría
DOI
10.11606/D.23.2007.tde-02012008-122236
Documento
Autor
Nombre completo
Ronald Vargas Orellana
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2007
Director
Tribunal
Dias, Reinaldo Brito e (Presidente)
Geraldini, Cleusa Aparecida Campanini
Montagna, Maria Cecilia
Título en portugués
Avaliação das propriedades mecânicas de um silicone de cura acética com adição de silicato de magnésio
Palabras clave en portugués
Prótese Facial
Silicato de magnésio
Silicone
Talco
Resumen en portugués
Os silicones requerem várias caraterísticas e requisitos para seu uso na confecção de próteses faciais, principalmente, referente a textura da pele; para alcançar essa meta devem ser adicionados outros materiais. O objetivo deste trabalho foi avaliar as propriedades mecânicas de um silicone nacional RTV. de cura acética, disponível no mercado, adicionando silicato de magnésio (talco). O material foi estudado em seu estado original e com acréscimo de 10% e 20% de silicato de magnésio. Foi submetido a testes de alongamento de ruptura, resistência à tração ou tensão de ruptura e de resistência ao rasgamento. Após a avaliação individual dos corpos de prova, obteve-se uma média total de cada grupo e submeteu-se a estudo comparativo frente aos resultados obtidos por meio de análise de variância (ANOVA) e teste de Tukey. O silicone em estado original mostrou-se mais resistente ao alongamento. O silicone com adição de 10 % de silicato de magnésio modificou suas propriedades mecânicas e obteve maior resistencia à tração. O silicone com adição de 20 % de silicato magnésio obteve maior resistência ao rasgamento. O silicone em que foi adicionado 10 % de silicato de magnésio de maneira geral obteve os valores mais significativos nas três propriedades testadas, o que indica que adicionando mais de 10 % diminui as propriedades mecânicas gradualmente, tornando-se inversamente proporcionais.
Título en inglés
Evaluation of the mechanical properties of the cured acetic silicone added with magnesium silicate
Palabras clave en inglés
Facial prosthesis
Rubber silicone
Silicate of magnesium
Talc
Resumen en inglés
The silicones request many characteristics and requirements for the use in the making of facial prostheses. To reach that objective other materials should be added. The aim of this work was to evaluate the mechanical properties of a national acetic cure silicone RTV, available in the market, adding silicate of magnesium (talc). The material was studied in your natural state and with increment of 10% and 20% of silicate of magnesium. It was submitted to tests of elongation and break, tensile strength and tear strength. After the individual evaluation of the specimens, it was obtained measured total of the each group and submitted to study comparative front to the results obtained through variance analysis (ANOVA) and Tukey test. The silicone in been original it showed to be more resistant to the elongation. The silicone with addition of 10% of silicate of magnesium modified your mechanical properties and obtained larger tear resistance. The silicone with addition of 20% of silicate magnesium obtained larger resistance to the tear strength. The silicone in witch it added 10% of silicate of magnesium in general obtained the more significant values in the three tested properties; that means that the increment of more than 10% lesses the properties gradually, becoming inversely proportional.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
RonaldVargasOrellana.pdf (479.16 Kbytes)
Fecha de Publicación
2008-06-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.