Mémoire de Maîtrise
DOI
10.11606/D.25.2009.tde-01062009-150441
Document
Auteur
Nom complet
Polliana Mendes Cándia Scaffa
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Bauru, 2009
Directeur
Jury
Mondelli, Rafael Francisco Lia (Président)
Coutinho, Margareth da Silva
Francischone, Carlos Eduardo
Titre en portugais
Efeito de diferentes tratamentos de superfície na resistência de união de um cimento resinoso à zircônia
Mots-clés en portugais
Cimento resinoso
Jateamento com Al2O3
MDP
Resistência de união
Revestimento com sílica
Tratamentos de superfície
Zircônia (Y-TZP)
Resumé en portugais
As ceramicas a base de zirconia (Y-TZP) apresentam propriedades mecanicas superiores as das demais ceramicas odontologicas. Entretanto, o aumento do conteudo cristalino modificou suas caracteristicas de adesao a cimentos resinosos, tornando necessario o desenvolvimento de metodos mais efetivos de uniao a estes materiais. Este trabalho in vitro pretende, portanto, avaliar a influencia de diferentes tratamentos de superficie e de diferentes agentes de uniao na resistencia ao cisalhamento entre uma zirconia estabilizada por itrio e um agente cimentante autoadesivo (RelyX U100®/3M ESPE). Para tal, cilindros de PROCERA® Allzircon receberam como tratamento de superficie jateamento com oxido de aluminio (Al2O3 - 50 m) ou jateamento com o sistema Rocatec. Sobre a superficie tratada dos cilindros foram aplicados, de acordo com os diferentes grupos experimentais, o sistema adesivo Clearfil SE Bond® (Kuraray Co.), e os primers Metal Zirconia Primer (Ivoclar Vivadent) e Alloy Primer (Kuraray Co.) e, finalmente, o cimento resinoso adotado. Cada especime foi, entao, submetido ao teste de cisalhamento (0,05 mm/min), por meio da acao de uma alca de fio ortodontico passando o mais próximo possivel da interface adesiva. A analise de variancia a um criterios (ANOVA) e o teste de Tukey (p<0,05) mostraram que a realizacao do tratamento de superfície aumentou os valores de resistencia de uniao entre a ceramica e o cimento resinoso. O jateamento com o sistema Rocatec (15,33 MPa) apresentou valores significantemente maiores que o jateamento com Al2O3 (11,93 MPa). A aplicacao dos agentes de uniao resultou em uma maior resistencia adesiva, sendo que o sistema adesivo Clearfill SE Bond (17,07 MPa) teve um comportamento estatisticamente superior aos demais materiais. Entre os primers, o Metal Zirconia Primer (11,26 MPa) apresentou maior valor de resistencia de uniao que o Alloy Primer (10,01 MPa). Portanto, a associacao de um tratamento superficial com um agente de união e valida, ja que promoveu os maiores valores de resistencia adesiva.
Mots-clés en anglais
Airborne abrasion with Al2O3
Bond strength
Resin cement
Silica coating
Surface treatments
Zirconia (Y-TZP)
Resumé en anglais
Yttrium-stabilized tetragonal zircon polycrystal (Y-TZP) ceramics show better mechanical properties than other dental ceramics. However, the high crystalline content modified their adhesiveness to resin cements, making it extremely necessary to develop a more effective adhesive strategy between them. This in vitro study intends to evaluate the influence of different surface treatments and different bond agents on the shear bond strength between a Y-TZP and self-adhesive resin cement. PROCERA® Allzircon cylinders (3.5 mm in diameter) received a surface airborne abrasion treatment with 50 m aluminum-oxide (Al2O3) particles or with the Rocatec system. According to the experimental groups, the adhesive system Clearfil SE Bond® (Kuraray Co.), and the primers Metal Zirconia Primer (Ivoclar Vivadent) and Alloy Primer (Kuraray Co.) were applied on the treated surface of the cylinders, before the application of the adopted resin cement (RelyX U100®/3M ESPE). Each specimen was submitted to the shear bond strength test (0.5 mm/min), by the action of an orthodontic stainless steel ligature wire (0.5 mm in diameter) loop, wrapped around the resin cement, as close as possible to the adhesive interface. One way-ANOVA and Tukey´s post hoc tests (p<0.05) revealed that surface treatment increased bond strength between the ceramic and the resin cement. Silica coating with the Rocatec system (15.33 MPa) showed significantly higher values than airborne abrasion with Al2O3 (11.93 MPa). Application of all bond agents improved shear bond strength: adhesive system Clearfil SE Bond (17.07 MPa) showed better performance than the other evaluated materials, and Metal Zirconia Primer (11.26 MPa) showed higher bond strength values than Alloy Primer (10.01 MPa). Therefore, the association of a surface treatment with a bond agent is suitable, once it resulted in higher values of adhesive strength.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2009-06-02
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.