Mémoire de Maîtrise
DOI
10.11606/D.25.2001.tde-06082002-194937
Document
Auteur
Nom complet
Rosa Maria Viana de Braganca Garcez
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Bauru, 2001
Directeur
Jury
Araujo, Paulo Amarante de (Président)
Buzalaf, Marilia Afonso Rabelo
Freitas, Cesar Antunes de
Titre en portugais
Avaliação da liberação de flúor de resinas compostas em água e ciclagem de pH
Mots-clés en portugais
ciclagem de pH
Flúor
resinas compostas
Resumé en portugais
O flúor tem um papel importante na estrutura dentária diminuindo a desmineralização e potencializando a remineralização. É fundamental conhecer o comportamento dos materiais restauradores no que diz respeito a liberação de flúor, não só em água deionizada, mas também em condições de desafio ácido. O objetivo desse trabalho foi avaliar a liberação de flúor de 6 materiais restauradores, em dois meios de imersão, água deionizada e sistema de ciclagem de pH entre, por 15 dias. Os materiais utilizados foram o Vitremer(VIT), o Dyract (DYR), o Ariston (A), o Tetric Ceram (TET), o Definite (DEF) e o Z 100. Para cada material foram confeccionados 16 corpos-de-prova na forma de discos (11 mm de diâmetro e 1,5 mm de espessura), os quais foram armazenados individualmente em 4 ml de cada solução, sendo 8 para cada meio de imersão. Na ciclagem de pH, o material era mantido 6 horas na solução desmineralizante e 18 horas na solução remineralizante. As soluções foram trocadas diariamente e os espécimes armazenados durante 15 dias. A liberação de flúor foi medida em 0,5 ml de solução adicionada a igual volume de TISAB II. Para os materiais Z 100, DEF e TET em água deionizada, a liberação de flúor foi obtida pela técnica da difusão facilitada por HMDS, nos períodos de 1, 7 e 15 dias. A análise da concentração de flúor foi medida por eletrodo específico para flúor, acoplado ao aparelho analisador de pH/F¯. Todos os materiais liberaram mais flúor no sistema de ciclagem de pH, exceto o Ariston. O pico de liberação foi maior no 1º dia, declinando do 2º dia em diante, e alcançando níveis baixos e constantes a partir do 7 º ao 15º dia. Os resultados foram submetidos a análise de variância a 3 critérios e ao teste de Tukey (p<0,05), para as comparações múltiplas. A liberação total no período do experimento em ordem decrescente, em água deionizada, em µgF¯/mm2 , foi A (3,6603), VIT (1,7529), DYR (0,2481), TET (0,0140), DEF (0,0086) e Z 100 (0,0020) e em ciclagem de pH, VIT (3,4366), A (2,1422), DYR (1,0691), TET (0,0297), Z 100 (0,0067) e DEF (0,0063). Assim concluímos que os materiais apresentaram padrão semelhante de liberação de flúor, exceto o Ariston, que mostrou comportamento estável e liberação constante durante os 15 dias, nos dois meios de imersão. Na ciclagem de pH, houve uma tendência de liberação de flúor de todos os materiais.
Titre en anglais
Evaluation of the fluoride release from composed resins in water and in pH - cycling system.
Mots-clés en anglais
composite resins
Fluoride
pH cycling.
Resumé en anglais
The fluoride has an important function in the dental structure reducing the desmineralization and increase the remineralization. It is fundamental to know the behavior of the restoratives materials relative the fluoride release, not only in deionized water, but also in conditions of acid challenge. The aim of the present study was to determine the fluoride release from 6 restoratives materials, in two storage solutions: deionized water and pH-cycling system solution over 15 days. 16 discs (11 mm diameter and 1,5 mm thickness) of materials, Vitremer (VIT), Dyract (DYR), Ariston pHc (A), Tetric Ceram (TET), Definite (DEF) and Z 100 were prepared and suspended individually in 4 mL of each solution, in number of 8 for each medium which was changed every 24 hours. In the pH-cycling system the specimens were immersed 6 hours in the demineralizing solution (pH 4,3) and 18 hours in remineralizing solution (pH 7,0). The solutions were changed daily during a period of 15 days. The fluoride release was determined after buffering the solutions with an equal volume of TISAB II. For the materials Z 100, DEF, TET in deionized water, the fluoride concentration was obtained by the microdiffusion method (Taves) in the periods of 1, 7 and 15 days. The analysis of the fluoride ion concentration in the solutions was measured using a fluoride ion sensitive electrode and a potent iometer ion-analyzer pH/F¯. The results of fluoride concentration in solutions eretransformed into released fluoride amount per material area (µgF¯/mm 2 ). All the materials released more fluoride in the pH-cycling system, exception Ariston. The release peak was larger in the 1st day, dropped at the 2nd and then remained constant from 7º to 15th day. The Ariston showed stable behavior, with small variations along the experiment. The results were submited to statistical analysis by ANOVA and the diferences between the treatments by the Tukey test (p<0,05). In deionized water, fluoride release in mgF¯/mm 2 was A(3,6603), VIT(1,7529), DYR (0,2481), TET (0,0140), DEF (0,0086) and Z 100 (0,0020) and, in pH-cycling system VIT (3,4366), A (2,1422), DYR (1,0691), TET (0,0297), Z 100 (0,0067) and DEF (0,0063), during the whole experimental period.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
TESE.pdf (1.32 Mbytes)
Date de Publication
2004-11-12
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.