Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.25.2003.tde-06102004-144621
Document
Auteur
Nom complet
Anderson Pinheiro de Freitas
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Bauru, 2003
Directeur
Jury
Francisconi, Paulo Afonso Silveira (Président)
Cruz, Carlos Alberto dos Santos
Rubo, Jose Henrique
Titre en portugais
Avaliação 'in vitro' da influência de diferentes tratamentos superficiais em uma liga metálica à base de cobalto-cromo-molibdênio sobre a resistência ao cisalhamento da união ao cimento resinoso
Mots-clés en portugais
cimento resinoso
ligas metálicas
materiais dentários
Resumé en portugais
Para avaliar o efeito de diferentes tratamentos superficiais sobre a resistência ao cisalhamento da união entre uma liga metálica (Co-Cr-Mo - Remanium CD) e um cimento resinoso (Rely XTM) e analisar o tipo de fratura durante a separação dos espécimes, quarenta pares de discos metálicos foram fundidos, regularizados e polidos, submetidos a quatro ciclos térmicos (vácuo, 960ºC, 8 minutos) e divididos aleatoriamente em quatro grupos. Cada grupo recebeu um tipo de tratamento: Grupo PSP: Polimento com lixa d'água Nº 600; Grupo PCP: Polimento com lixa 600 e aplicação do condicionador metálico Alloy Primer (Kuraray); Grupo JSP: Jato de óxido de alumínio (100 m, 75lib/pol2) e Grupo JCP: Jato de óxido de alumínio (100 m, 75lib/pol2) e aplicação do Alloy Primer. Os grupos foram cimentados e armazenados em água deionizada a 37ºC por 36 horas e separados em ensaio de cisalhamento. Os maiores valores foram produzidos pelos grupos jateados (JSP, JCP), independentemente da aplicação do primer; o Alloy Primer aumentou a retentividade entre o cimento Rely X e a superfície polida da liga de Co-Cr-Mo, entretanto sua força de união não superou a alcançada através do jateamento; todos os espécimes apresentaram falha adesiva na interface testada.
Resumé en anglais
To evaluate the effect of different surface treatments on shear bond strength between a metallic alloy (Co-Cr-Mo - Remanium CD) and a resin cement (Rely XTM) and to evaluate the mode of fracture after testing, forty couples of metallic-alloy disks were melted, regularized, polished, submitted to four thermal cycles at 960ºC and divided casually in four groups. Each group received a type of different treatment: Group PSP: Polishing with sandpaper 600; Group PCP: Polishing with sandpaper 600 and application of a metallic Primer; Group JSP: Sandblaster with 100 m aluminum oxide; Group JCP: Sandblaster with 100 m aluminum oxide and application of a metallic Primer. The groups were cemented and stored in distilled water at 37ºC for 36 hours and submitted to shear strength test. The highest values were obtained by the sandblasted groups (JSP, JCP), independently of the primer application; the Alloy Primer increased the retention between the Rely X cement and the polished surface of the Co-Cr-Mo alloy, however its bond strength was not greater than that obtained by sandblasting; all of the specimens showed adhesive failures within the tested interface.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2004-11-12
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.