• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
10.11606/D.25.2005.tde-16082005-114454
Documento
Autor
Nombre completo
Juliana Felippi David e Goés de Azevedo
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2005
Director
Tribunal
Mondelli, Rafael Francisco Lia (Presidente)
Andrade, Marcelo Ferrarezi de
Pereira, Jose Carlos
Título en portugués
Avaliação do desgaste e da rugosidade superficial do esmalte bovino submetido ao clareamento e escovação simulada
Palabras clave en portugués
desgaste
esmalte dentário
Resumen en portugués
Este estudo avaliou o desgaste e a alteração de rugosidade superficial do esmalte bovino submetido a três diferentes técnicas clareadoras e escovação simulada. Fragmentos de esmalte com 1,5cm x 0,5cm e altura de 0,4cm foram obtidos. Metade dessa porção de esmalte recebeu tratamento clareador e escovação simulada, ficando a outra metade como controle. Foram polidos seqüencialmente e a rugosidade aritmética (Ra) inicial determinada pela média (µm) de 5 leituras com o rugosímetro Hommel Tester T 1000. Os espécimes foram divididos em quatro grupos (n=10), de acordo com o tratamento empregado: G1= saliva artificial (controle); G2= peróxido de hidrogênio (PH) 35% (Lase Peroxide, DMC Equipamentos) ativado com luz híbrida (LED e laser de diodo) Ultrablue IV (DMC Equipamentos). O PH foi aplicado, aguardando-se 2 min para ser irradiado com a luz híbrida por 3 min e mantido sobre o espécime por mais 3 min, com 3 aplicações consecutivas; G3= PH 35% ativado com luz halógena Curing Light (3M/ESPE Dental Products). O PH foi aplicado, com tempo de espera de 2 min, para ser irradiado com luz halógena por 30s, intervalo de 30s, até completar 3 min de ativação, sendo o agente mantido sobre o espécime por mais 3 min, com 3 aplicações consecutivas; G4= clareamento com peróxido de carbamida (PC) 16% (Whitenees Perfect 16%, FGM) por 2h diárias durante 14 dias. Os espécimes foram imersos em saliva artificial pelo restante do tempo. Após o clareamento, a rugosidade (Ra) foi determinada e os corpos-de-prova armazenados em saliva artificial por 7 dias, com troca diária para remineralização, e submetidos a 100.000 ciclos de escovação simulada. Posteriormente, foram determinados a rugosidade final (Ra) e o desgaste superficial, o qual foi verificado pela média de três leituras, utilizando a perfilometria através do rugosímetro Hommel Tester T 1000. As médias de rugosidade superficial foram submetidas à análise de variância a 2 critérios e teste de Tuckey que não detectou diferenças significantes entre os grupos para a rugosidade inicial e após clareamento. Após a escovação, houve diferenças significantes entre o grupo controle e os demais grupos, em que o G4 apresentou aumento significante da rugosidade em relação ao G2. As médias de desgaste foram submetidas à análise de variância e teste de Tuckey, onde o G1 apresentou menor desgaste que os demais grupos. As técnicas de clareamento dental empregadas na superfície de esmalte bovino proporcionaram aumento da rugosidade e do desgaste superficial, quando submetido à escovação simulada.
Resumen en inglés
The purpose of this study was to evaluate the surface roughness and wear of bovine enamel submitted to three different bleaching techniques (two in-office and one home bleaching) and simulated brushing. Enamel fragments (1.5cm x 0.5cm and 0.4cm high) were obtained. Half of each specimen was treated with a bleaching agent and submitted to simulated brushing, and the other half was used as control. The specimens were polished and five readings of initial surface roughness were carried out using a perfilometer (Hommel Tester T 1000). The average surface roughness (Ra) was obtained. The specimens were randomly divided into 4 groups (n=10) according to treatment: G1= artificial saliva (control); G2= 35% hydrogen peroxide (HP) (Lase Peroxide, DMC Equipments), activated with a hybrid light (LED and Diode laser) Ultrablue IV (DMC Equipments); G3= 35% HP (Lase Peroxide) activated with halogen light (Curing Light-3M ESPE). The 35% hydrogen peroxide agent was applied on the enamel surface for three consecutive times; G4= 16% PC bleaching agent (Whiteness Perfect, FGM) for 2 hours daily during 14 days. The samples were stored in artificial saliva for the remaining time. After bleaching treatment, the surface roughness (Ra) was measured and the specimens were stored in artificial saliva for 7 days, and then subjected to 100,000 cycles of simulated brushing. The final roughness (Ra) was determined and three readings of superficial wear were carried out (Hommel Tester T 1000). The superficial roughness average values were statistically analyzed by two-way ANOVA and Tukey test. There were no significant differences among groups comparing initial and pos-bleaching roughness. After brushing, there were significant differences between control group and experimental groups. G4 showed a significant increase in roughness values compared to G2. Wear was significantly less for G1 compared to other groups (one-way ANOVA and Tukey test). Bleaching techniques promote increased bovine enamel surface roughness and superficial wear, when submitted to simulated brushing.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2005-08-22
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.