Disertación de Maestría
DOI
10.11606/D.25.2005.tde-20032006-111501
Documento
Autor
Nombre completo
Adilson Yoshio Furuse
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2005
Director
Tribunal
Mondelli, Jose (Presidente)
Francischone, Carlos Eduardo
Garone Filho, Wilson
Título en portugués
Efeito de diferentes tratamentos de superfície na resistência de união adesiva em resina composta contaminada por saliva
Palabras clave en portugués
resinas compostas
resistência de união (odontologia)
saliva
Resumen en portugués
Avaliou-se a resistência adesiva ao cisalhamento de uma resina composta contaminada por saliva, com adição de novo incremento do mesmo material. 40 corpos-de-prova de uma resina composta nano-híbrida, confeccionados em uma matriz de resina epóxica, foram divididos em quatro grupos, cada um recebendo um tratamento de superfície. Em um dos grupos, a superfície não foi contaminada (Grupo 1 - controle). Para a confecção do segundo segmento do corpo-de-prova, utilizou-se uma matriz de Teflon de 3,5mm de diâmetro por 3,0mm de altura. Nos demais grupos, a superfície da resina composta foi contaminada com saliva e seca com ar comprimido, sendo os tratamentos estabelecidos da seguinte forma: Grupo 2 - resina composta inserida e polimerizada sobre a superfície contaminada; Grupo 3 - condicionamento com ácido fosfórico a 35%, aplicação de adesivo e inserção de resina composta; Grupo 4 - asperização com ponta diamantada, condicionamento com ácido fosfórico a 35%, aplicação de adesivo e inserção de resina composta. Após a confecção, os espécimes foram armazenados em água a 37oC durante 24h, sendo em seguida montados em uma máquina universal de ensaios para realização dos testes de resistência ao cisalhamento. Os resultados foram submetidos à análise de variância a um critério e ao teste de Tukey para comparação entre os grupos. Não houve diferença entre os grupos 3, 4 e controle (p < 0,05). A contaminação da superfície da resina com saliva (Grupo 2) diminuiu significativamente a resistência de união (p < 0,05). A análise em MEV dos espécimes do grupo 2 demonstrou a ocorrência de fraturas na interface adesiva em quase todos os corpos-de-prova (80%). Fraturas coesivas da resina inserida na matriz de resina epóxica puderam ser observadas em todos os espécimes dos Grupos 3 e 4. O método que emprega limpeza superficial com ácido e aplicação de um sistema adesivo demonstrou ser efetivo na recuperação da resistência adesiva a valores semelhantes à resistência coesiva do material
Título en inglés
EFFECT OF DIFFERENT SURFACE TREATMENTS IN SHEAR BOND STRENGTH OF COMPOSITE RESIN CONTAMINATED BY SALIVA
Resumen en inglés
Shear bond strength between the contaminated composite resin surface and a new increment of the same material was analysed. Forty specimens of a nanohybrid composite, were divided into four groups. Each group received a surface treatment. In one of the groups, there was no surface contamination (Group 1 - control). The new increment of composite resin was inserted by placing a Teflon matrix (3.5mm height, 3mm diameter) over the already polymerized composite surface. For the other groups, the polymerized composite surface was contaminated with saliva and dried with air. Surface treatments were performed in the following way: Group 2 - new increment was inserted and polymerized directly on the contaminated surface; Group 3 - contaminated surface was treated with 35% phosphoric acid etching and adhesive was applied prior to the insertion of the new increment; Group 4 - diamond bur roughening, 35% phosphoric acid etching, adhesive application and insertion of the new composite increment. Specimens were stored in water at 37oC for 24h. After this period, specimens were mounted in a universal testing machine for the shear bond strength tests. Results were submitted to one way anova and Tukey test multiple comparison. No significant differences were detected between Groups 3, 4 and control (p < 0.05). Saliva contamination of resin surface (Group 2) significantly reduced shear bond strength (p < 0.05). SEM analysis in Group 2 demonstrated fractures at the interface in 80% of the specimens. Cohesive fractures in first increment of resin composite was observed in all specimens in Groups 3 and 4. Decontamination of resin surface with phosphoric acid followed by adhesive application, was an effective method to improve shear strength, reaching similar numbers to the cohesive resistance of the material
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2006-04-06
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.