Disertación de Maestría
DOI
10.11606/D.25.2007.tde-23082007-112135
Documento
Autor
Nombre completo
Fabiane Lopes Toledo
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2007
Director
Tribunal
Freitas, Cesar Antunes de (Presidente)
Mondelli, Jose
Segalla, Jose Claudio Martins
Título en portugués
Resistência à remoção por tração de coroas NiCr cimentadas sobre munhões usinados em liga de titânio, irradiados ou não por LASER
Palabras clave en portugués
cimentação
implante dentário
resistência à tração
Resumen en portugués
No presente trabalho, usando ensaios de remoção por tração, o objetivo foi avaliar a eficiência de 4 agentes (fosfato de zinco S. S.White, ionômero de vidro Ketac Cem Easymix, resina composta RelayX Luting 2 e resina acrílica especial Panavia 21 TC) usados para fixar coroas totais de NiCr a munhões tronco-cônicos, usinados em liga de Ti-6Al-4V. Dentre os cinqüenta munhões utilizados, 40 permaneceram com sua superfície original altamente lisa (como vieram de fábrica) e foram distribuídos em grupos de 10, para cada agente cimentante; no grupo dos 10 restantes existiu uma modificação por irradiação com LASER e cimentação apenas com fosfato. Os ensaios mecânicos foram realizados em uma máquina universal MTS 810, na velocidade de 0,5 mm/min. A respectiva Análise de Variância (ANOVA) apontou existir diferença significante entre os grupos e o teste de Tukey (p<0,05) também mostrou diferenças significantes entre eles, exceto nas comparações original/fosfato versus original/RelayX e original/fosfato versus original/KetcCem. Para os munhões não-irradiados, o melhor desempenho foi apresentado pela resina Panavia 21 (1.127,996 N); a resina composta RelyX (478,197 N) mostrou comportamento similar apenas ao do fosfato (430,662 N), o qual apresentou desempenho semelhante ao ionômero de vidro KetacCem (227,705 N). A modificação da superfície do munhão fez com que a magnitude da resistência à tração das coroas cimentadas com fosfato aumentasse para 1.514,872 N.
Título en inglés
Tensile strenght of NiCr crowns cemented upon usinated titanium alloy abutments, LASER irradiated or not
Palabras clave en inglés
cementation
dental implantation
tensile strenght
Resumen en inglés
By means of tensile essays, NiCr total crowns were removed from usinated tronco-conical abutments composed by an Ti-6Al-4V alloy; the performance of 4 cementig agents (S. S. White zinc phoshate, Ketac Cem Easymix glass ionomer, RelayX Luting 2 composite resin and Panavia 21 TC special acrylic resin) was evaluated. Among a total of 50 abutments, 40 were used with it surface presenting high smoothness (as they come from manufacturer) and distributed in groups of 10 elements, each group for each cementing agent; the other 10 abutments had had its surfaces modified by LASER and were used only with phosphate. The mechanical essays were developed at a MTS 810 universal machine, adjusted to a 0.5 mm/m velocity. The ANOVA applied to data pointed out the existence of significant differences between groups; the subsequent Tukey´s test (p<0.05) also detected significant differences, except at comparisons of original/phosphate versus original/ RelayX and original/phosphate versus original/ KetacCem. To non-irradiated abutments, the better performance was presented by Panavia 21 (1,127.996 N); RelyX (478.197 N) showed itself similar only to phosphate (430.662 N), wich had a performance similar to that of KetacCem (227.705 N). The referred LASER irradiation promoted an increased resistance to the phosfate, which reached 1,514.872 N.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
FabianeToledo.pdf (2.10 Mbytes)
Fecha de Publicación
2007-08-23
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.