Tesis Doctoral
DOI
10.11606/T.25.2002.tde-23082011-093619
Documento
Autor
Nombre completo
Paulo Humaitá de Abreu
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2002
Director
Tribunal
Mondelli, Jose (Presidente)
Araujo, Paulo Amarante de
Marchese, Marco Polo
Nunes, Osvaldo Benoni da Cunha
Veronezi, Maria Cecilia
Título en portugués
Resistência à corrosão de amálgamas e de liga à base de gálio, sem e com adesivos, através do método de perda de peso e análise da rugosidade de superfície.
Palabras clave en portugués
Amálgama dentário
Corrosão dentária
Gálio
Restauração dentária
Resumen en portugués
Avaliou-se a resistência à corrosão pelos testes de perda de peso em imersão alternada (solução-ar) e as conseqüentes alterações produzidas nas superfícies dos três materiais restauradores (os amálgamas Dispersalloy e Tytin Plus, ambos de alto conteúdo de cobre, respectivamente do tipo fase dispersa e do tipo partícula única, assim como a liga à base de gálio Galloy), não ou associados a dois sistemas adesivos (All-Bond 2 e PAAMA-2), observadas através da medição da rugosidade de superfície. Confeccionou-se dez corpos-de-prova, para cada condição específica, a partir de uma matriz metálica de aço inoxidável contendo cinco cavidades cilíndricas, com 10,7 mm de diâmetro por 3,0 mm de altura cada uma. Após o polimento, como é feito no caso de análises metalográficas, os espécimes foram pesados e levados ao rugosímetro para realizar as medições imediatamente. Estes foram submetidos à imersão alternada, na solução de sulfeto de sódio a 5 %, por um período de 24 horas e novamente foi realizada a pesagem e obtidos os valores de perda de peso. Depois da pesagem, os corpos-de-prova foram levados novamente ao rugosímetro para obtenção dos valores médios de rugosidade de superfície. Os resultados foram registrados e submetidos à análise de variância, a dois critérios, e ao teste de contrastes de Tukey-Kramer. Dos resultados obtidos, conclui-se que todos os espécimes perderam peso e tiveram sua rugosidade de superfície aumentada após a imersão em solução corrosiva; a liga Galloy mostrou valores maiores, tanto no método de perda de peso como no de rugosidade de superfície, quando comparada aos dois amálgamas; a liga Tytin Plus alcançou os melhores resultados; houve diferença estatisticamente significante entre os materiais restauradores, mas não entre os sistemas adesivos utilizados, mostrando comportamentos diferentes dependendo da combinação desses fatores.
Palabras clave en inglés
Dental amalgam
Dental etching
Dental restoration
Gallium
Resumen en inglés
The resistance to the corrosion was evaluated through weight loss to an alternated immersion (solution-air) and its consequent changes on the surface of three restoring materials (them amalgams Dispersalloy and Tytin Plus, both with high copper content, respectively dispersion phase and unique particle, as well as the alloy gallium base Galloy), associated or not to two adhesive systems (All-Bond 2 and PAAMA-2), observed by measuring the surface roughness. Ten bodies-of-test were made, for each specific condition, in a metallic matrix os stainlesss steel with five cilindrical cavities, measuring 10,7 mm in diameter and 3,0 mm thickness each one. After polishing, as in the metalographic anal ysis, the specimens were weighed and submitted to the roughness measurer to measuring inicial. These were submitted to an alternated immersion in 5 % sodium sulfide solution, for 24 hours and then the second weighting was performed and obtained the average values of weight loss. A second measure of the surface roughness was then performed. The results were registered and submitted to the variance analysis, to two approaches, and to the test of contrasts of Tukey-Kramer. From the obtained results, it was concluded that all specimens lost weight and there was an increasing roughness surface after immersion in corrosive solution; Galloy showed higher values, both weight loss test and the rougness surface, compared to two amalgams; the alloy Tytin Plus obtained better results; there was significant statistical difference among the restoring materials, but not among adhesive systems, showing different behaviors according to arrangement of these factors.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
PauloHumaitadeAbreu.pdf (211.39 Kbytes)
Fecha de Publicación
2011-08-25
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.