Disertación de Maestría
DOI
10.11606/D.25.2007.tde-27082007-142314
Documento
Autor
Nombre completo
Leandro de Moura Martins
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2007
Director
Tribunal
Francisconi, Paulo Afonso Silveira (Presidente)
Araujo, Paulo Amarante de
Rastelli, Alessandra Nara de Souza
Título en portugués
Avaliação da microdureza Knoop e do grau de conversão de dois cimentos de ionômero de vidro modificados por resina em função do tipo de polimerização e do tempo
Palabras clave en portugués
Cimentos de ionômeros de vidro modificado por resina
Espectroscopia FT-IR
Microdureza Knoop
Polimerização
Tempo de armazenagem
Resumen en portugués
Os ionômeros de vidro vêm sendo utilizados largamente na odontologia com diversas funções. Suas formulações sofreram alterações durante os anos, como a incorporação de componentes resinosos, para a melhoria de suas propriedades físicas e aumento do tempo de trabalho. Com isso, o estudo teve como objetivo avaliar o grau de conversão e a microdureza Knoop dos cimentos de ionômero de vidro modificados por resina (Rely X Luting e Vitremer, ambos da 3M ESPE) de acordo a forma de polimerização (química ou fotopolimerável por lâmpada halógena Ultralux EL ? Gnatus e LED LEC 1000 ? MMOptics) e o tempo de armazenagem. Três espécimes de cada material, autopolimerizável e fotopolimerizável, e tipo de fotopolimerização (por luz halógena e LED) foram confeccionados para cada tempo experimental de 6 horas, 1, 2, 3, 5, 7 ,11 e 14 dias (n=72). Os espécimes foram armazenados em ambiente escuro a 37°C durante esses períodos. Os 72 espécimes foram analisados pela espectroscopia FT-IR para a medição do grau de conversão (GC). Três espécimes de cada material e tipo de polimerização (n=9) foram confeccionados para a medição da microdureza, com um penetrador diamantado piramidal, tipo Knoop, carga estática de 50 gramas por 30 segundos. Os resultados encontrados demonstraram que o material fotopolimerizado com LED apresentou os maiores valores do grau de conversão e da microdureza. O grau de conversão aumentou com o tempo de armazenagem enquanto a microdureza obteve os maiores resultados entre 24-48 horas. Os resultados permitiram concluir que para os cimentos de ionômero de vidro modificados por resina, Vitremer e Rely X Luting, o material fotopolimerizável onde se utilizou o LED apresentou os melhores resultados e que a microdureza Knoop foi ineficaz para predizer o grau de conversão.
Título en inglés
Evaluation of the Knoop microhardness and the degree of conversion of two resin-modified glass ionomer in function of the type of polymerization and the time
Palabras clave en inglés
FT-IR spectroscopy Knoop microhardness
Polymerization
resin modified glass ionomer cements
Storage time
Resumen en inglés
Glass ionomer cement have been widely used for many functions. Over the years, some alterations have been made to improve some physico-mechanical properties and to prolong working time. The purpose of this study was to evaluate the relation of the degree of conversion (DC) and Knoop microhardness of resin modified glass ionomer cements (Rely X Luting and Vitremer - 3M ESPE) with polymerization type (chemical curing and light curing reactions, using halogen light or LED) and time of storage. Three specimens of each material, self-cured and light-cured, and light-curing type (halogen light or LED) were prepared for each period of time (n=72). Specimens were stored in dark and dry conditions, at 37oC, during 6 hours, 1, 2, 3, 5, 7, 11 and 14 days. All the specimens were analyzed by FT-IR spectroscopy to measure the DC. Three specimens of each material and polimeryzation type (n=9) were prepared for the microhardness determination, equipped with a Knoop indenter, 50g load for 30 seconds. Results showed that higher values of DC and Knoop microhardness were found on the LED light-cured material. DC values increased with storage time while the Knoop microhardness achieved its higher values between 24-48 hours. Results showed that the LED light-curing unit used to polymerize the resin modified glass ionomer cement Vitremer achieved better values of DC, between light and self-cured materials, and that the Knoop microhardness could not predict the DC.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
LeandroMartins.pdf (2.40 Mbytes)
Fecha de Publicación
2007-08-27
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.