Tesis Doctoral
DOI
10.11606/T.25.2005.tde-28092005-113328
Documento
Autor
Nombre completo
Anderson Pinheiro de Freitas
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2005
Director
Tribunal
Francisconi, Paulo Afonso Silveira (Presidente)
Araujo, Paulo Amarante de
Carvalho Júnior, Oscar Barreiros de
Rubo, Jose Henrique
Santos Júnior, Gildo Coelho
Título en portugués
Avaliação da influência do tratamento superficial e do condicionador sobre a resistência ao cisalhamento da união entre uma liga de Co-Cr-Mo e reparos em resina composta
Palabras clave en portugués
gomas e resinas
materiais dentários
Resumen en portugués
Para avaliar o efeito de diferentes tratamentos superficiais sobre a resistência ao cisalhamento da união entre uma liga metálica (Co-Cr-Mo - Remanium CD) e uma resina composta (Z-250) e analisar o tipo de fratura durante a separação dos espécimes, sessenta discos metálicos foram fundidos, regularizados e polidos, submetidos a quatro ciclos térmicos (vácuo, 960ºC, 8 minutos) e divididos aleatoriamente em seis grupos. Cada grupo recebeu um tipo de tratamento: Grupo ASB: Asperização com ponta diamantada (No 3118); Grupo ASI: Asperização e aplicação do silano (3M); Grupo AAP: Asperização e aplicação do Alloy Primer (Kuraray); Grupo JSB: Jateamento com óxido de alumínio (50µm, 75lib/pol2); Grupo JSI: Jateamento e aplicação do silano; Grupo JAP: Jateamento e aplicação do Alloy Primer. Todos os espécimes receberam aplicação do adesivo Single Bond e da resina Z-250 (3M), foram armazenados em água deionizada a 37ºC por 24 horas e separados em ensaio de cisalhamento. Os resultados e desvio-padrão de cada grupo, expressos em MPa foram: ASB: 12,708±2,962; ASI: 16,343±2,714 e AAP: 16,723±2,666; JSB: 25,958±5,650; JSI: 28,185±3,322; JAP: 28,670±3,246. Os maiores valores foram produzidos pelos grupos jateados (JSB, JSI e JAP); o silano e o Alloy primer aumentaram a retentividade entre a resina Z-250 e a liga de Co-Cr-Mo, independente da textura superficial e sem apresentar diferença entre os mesmos; todos os espécimes apresentaram falha adesiva na interface testada.
Palabras clave en inglés
Composite resin
Metallic alloy
Primer
Shear bond strength
Silane
Surface treatment
Resumen en inglés
To evaluate the effect of different surface treatments on shear bond strength between a metallic alloy (Co-Cr-Mo - Remanium CD) and a composite resin (Z-250) and to evaluate the fracture mode after testing, sixty disks were casted, polished, submitted to four thermal cycles (960ºC/8min) and divided randomly in six groups. Each group received a different type of treatment: Group ASB: roughen with diamond bur (No 3118); Group ASI: roughen and application of a ceramic Primer; Group AAP: roughen and application of a metallic Primer; Group JSB: Sandblasting with 50 µm aluminum oxide (75lib/pol2); Group JSI: Sandblasting and application of a ceramic Primer; Group JAP: Sandblasting and application of a metallic Primer. All the specimens received the application of an adhesive (Single Bond) and a composite resin (Z-250 /3M). The groups were stored in distilled water at 37ºC during 24 hours and submitted to shear bond strength test. The results and the standard deviation of each group (expressed in MPa) were: JSB: 25,958±5,650; JSI: 28,185±3,322; JAP: 28,670±3,246; ASB: 12,708±2,962; ASI: 16,343±2,714 and AAP: 16,723±2,666. The highest values were obtained by the sandblasted groups (JSB, JSI e JAP). In spite of the surface, ceramic primer and alloy primer increased the retention between the composite resin Z-250 and the Co-Cr-Mo alloy without statistical differences on the results; all of the specimens showed adhesive failures.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2005-10-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.