Thèse de Doctorat
DOI
10.11606/T.25.2005.tde-28092005-113328
Document
Auteur
Nom complet
Anderson Pinheiro de Freitas
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Bauru, 2005
Directeur
Jury
Francisconi, Paulo Afonso Silveira (Président)
Araujo, Paulo Amarante de
Carvalho Júnior, Oscar Barreiros de
Rubo, Jose Henrique
Santos Júnior, Gildo Coelho
Titre en portugais
Avaliação da influência do tratamento superficial e do condicionador sobre a resistência ao cisalhamento da união entre uma liga de Co-Cr-Mo e reparos em resina composta
Mots-clés en portugais
gomas e resinas
materiais dentários
Resumé en portugais
Para avaliar o efeito de diferentes tratamentos superficiais sobre a resistência ao cisalhamento da união entre uma liga metálica (Co-Cr-Mo - Remanium CD) e uma resina composta (Z-250) e analisar o tipo de fratura durante a separação dos espécimes, sessenta discos metálicos foram fundidos, regularizados e polidos, submetidos a quatro ciclos térmicos (vácuo, 960ºC, 8 minutos) e divididos aleatoriamente em seis grupos. Cada grupo recebeu um tipo de tratamento: Grupo ASB: Asperização com ponta diamantada (No 3118); Grupo ASI: Asperização e aplicação do silano (3M); Grupo AAP: Asperização e aplicação do Alloy Primer (Kuraray); Grupo JSB: Jateamento com óxido de alumínio (50µm, 75lib/pol2); Grupo JSI: Jateamento e aplicação do silano; Grupo JAP: Jateamento e aplicação do Alloy Primer. Todos os espécimes receberam aplicação do adesivo Single Bond e da resina Z-250 (3M), foram armazenados em água deionizada a 37ºC por 24 horas e separados em ensaio de cisalhamento. Os resultados e desvio-padrão de cada grupo, expressos em MPa foram: ASB: 12,708±2,962; ASI: 16,343±2,714 e AAP: 16,723±2,666; JSB: 25,958±5,650; JSI: 28,185±3,322; JAP: 28,670±3,246. Os maiores valores foram produzidos pelos grupos jateados (JSB, JSI e JAP); o silano e o Alloy primer aumentaram a retentividade entre a resina Z-250 e a liga de Co-Cr-Mo, independente da textura superficial e sem apresentar diferença entre os mesmos; todos os espécimes apresentaram falha adesiva na interface testada.
Mots-clés en anglais
Composite resin
Metallic alloy
Primer
Shear bond strength
Silane
Surface treatment
Resumé en anglais
To evaluate the effect of different surface treatments on shear bond strength between a metallic alloy (Co-Cr-Mo - Remanium CD) and a composite resin (Z-250) and to evaluate the fracture mode after testing, sixty disks were casted, polished, submitted to four thermal cycles (960ºC/8min) and divided randomly in six groups. Each group received a different type of treatment: Group ASB: roughen with diamond bur (No 3118); Group ASI: roughen and application of a ceramic Primer; Group AAP: roughen and application of a metallic Primer; Group JSB: Sandblasting with 50 µm aluminum oxide (75lib/pol2); Group JSI: Sandblasting and application of a ceramic Primer; Group JAP: Sandblasting and application of a metallic Primer. All the specimens received the application of an adhesive (Single Bond) and a composite resin (Z-250 /3M). The groups were stored in distilled water at 37ºC during 24 hours and submitted to shear bond strength test. The results and the standard deviation of each group (expressed in MPa) were: JSB: 25,958±5,650; JSI: 28,185±3,322; JAP: 28,670±3,246; ASB: 12,708±2,962; ASI: 16,343±2,714 and AAP: 16,723±2,666. The highest values were obtained by the sandblasted groups (JSB, JSI e JAP). In spite of the surface, ceramic primer and alloy primer increased the retention between the composite resin Z-250 and the Co-Cr-Mo alloy without statistical differences on the results; all of the specimens showed adhesive failures.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2005-10-14
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.