Disertación de Maestría
DOI
10.11606/D.25.2009.tde-29052009-094511
Documento
Autor
Nombre completo
Juan Carlos Pontons Melo
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2009
Director
Tribunal
Freitas, Cesar Antunes de (Presidente)
Francisconi, Paulo Afonso Silveira
Sábio, Sérgio
Título en portugués
Avaliação do desgaste por escovação, in vitro, de uma resina composta, fotopolimerizada por lâmpada halógena, em dois diferentes tempos
Palabras clave en portugués
Abrasão
Desgaste
Escovação
Resina composta
Resumen en portugués
Um dos principais problemas dos materiais restauradores (incluindo a resina composta) é o desgaste por abrasão. Portanto, o objetivo neste trabalho foi avaliar in vitro o desgaste abrasivo por escovação da resina composta 4Seasons, de duas cores diferentes (A3 e C4) e com fotopolimerização por dois diferentes tempos (20 e 40 s), utilizando escova Sorriso, da Colgate, e creme dentifrício Colgate Tripla Ação; também foi usado, como material de referência, o polimetil metacrilato. Assim, foram confeccionados dez corpos-de-prova, para cada um dos cinco grupos formados (PMMA, A3 20s, A3 40s, C4 20s, C4 40s). Cada espécime consistia basicamente num cilindro de cerca de 1,8 mm de altura e 8 mm de diâmetro. Cada espécime, após sua confecção, era imerso em água deionizada, a 37 ± 2 ºC, por 24 horas, quando então eram regularizados com lixa (granulação # 600 e # 1.000); após lavagem com ultrassom, voltavam a ser armazenados nas mesmas condições, até completar-se um período de uma semana. A escovação foi então efetuada numa máquina própria, que comportava dez espécimes simultaneamente, sendo de 3 N a carga de cada escova sobre o respectivo espécime; a velocidade de cada escova era de 18 cm/s, com a freqüência (ida e volta, num percurso total de 4 cm) de 4,5 ciclos/s; o período de escovação de um espécime compreendia 150. 000 ciclos. Foram efetuados cinco períodos (ou lotes) de escovação, de modo que um espécime do material de cada grupo tivesse sido submetido à ação de cada uma das posições ocupadas pelas dez escovas. A quantidade de massa perdida, para cada espécime, foi calculada por meio de pesagem (pré e pós escovação), numa balança com acuidade de milionésimo de grama. O trabalho foi também ilustrado com gráficos de rugosidade e com fotomicrografias tomadas ao MEV. A taxa média de desgaste foi de 2,8 mg para o PMMA, de 5,5 mg para o A3-20s, 4,7 mg para o A3-40 s, 5,4 para o C4-20s e 4,2 mg para o C4-40s; a respectiva análise de variância mostrou não existir diferença significante entre os grupos, para p=0,166; o coeficiente de variação entre os grupos foi bastante semelhante. Foi possível concluir que não existiu diferença da resistência ao desgaste abrasivo entre os grupos estudados.
Título en inglés
In vitro toothbrushing wear evaluation of a resin composite cured by QTH curing unit in two different times
Palabras clave en inglés
Abrasion
Resin composite
Toothbrushing
Wear
Wear resistance
Resumen en inglés
One of the main problems of dental restorative materials (including the resin composites) is the abrasion wear. Therefore, the aim of this work was to evaluate in vitro the abrasive wear by toothbrushing of the resin composite 4Seasons, of two different colors (A3 and C4), cured by two different times (20 and 40 s), using a toothbrush (Sorriso - Colgate), and a dentifrice (Tripla Ação Colgate). Polimetil meth-acrylate was used as reference material. Ten cylindric samples (approximately 1.8 mm height and 8 mm diameter) had been prepared for each one of the five evaluated groups (PMMA, A3 20s, A3 40s, C4 20s, C4 40s). After confection, samples were immersed in deionized water, at 37 ± 2ºC, for 24 h, and then regularized by abrasive gritting with sandpaper (from #600 to # 1 000); after that, were cleaned in ultrasound bath, and restored to the same described conditions, until completing the period of one week. The toothbrushing was then conducted in a proper machine that holds 10 specimens simultaneously, with a 3 N load of each toothbrush on the respective sample. The speed of each toothbrush was of 18 cm/s, at a frequency of 4.5 cycles/s (each cycle consisting of 2 cm forward and 2 cm backward). 150. 000 cycles were applied per sample. Five periods (or lots) of toothbrushing had been performed, in a way that one sample of each group had been submitted to the brushing action at one position in the machine. The amount of weight loss for each sample was calculated by means of weighting (before and after toothbrushing), in an analytical balance with accuracy of millionth of gram. Roughness and MEV photomicrographies were also evaluated. The average rate of wear was of 2.8 mg for PMMA, 5.5 mg for A3-20s, 4.7 mg for A3-40 s, 5.4 for C4-20s, and 4,2 mg for C4-40s. One-way ANOVA showed no significant difference between groups (p = 0.166). The coefficient of variation between the groups was sufficiently similar. It was possible to conclude that difference of the resistance to the abrasive wear between the studied groups did not exist.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-06-02
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.