Disertación de Maestría
DOI
10.11606/D.25.2003.tde-21032005-092248
Documento
Autor
Nombre completo
Thais Marchini de Oliveira
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2002
Director
Tribunal
Abdo, Ruy Cesar Camargo (Presidente)
Aguiar, Sandra Maria Herondina Coelho Ávila de
Pavarini, Aymar
Título en portugués
Avaliação 'in vitro' da infiltração marginal de restaurações indiretas com resina composta em molares decíduos cimentadas com dois tipos de cimentos
Palabras clave en portugués
cimentos dentários
infiltração dentária
molar
resinas compostas
restauração indireta sem metal
Resumen en portugués
O objetivo deste trabalho foi avaliar “in vitro” a infiltração marginal em restaurações indiretas Classe II, realizadas com resina composta Filtek Z250 e cimentadas com dois tipos de cimentos: Enforce e RelyX Cimento Resinoso Adesivo. A amostra experimental constituiu-se de vinte e quatro segundos molares decíduos. Foram confeccionadas cavidades estritamente mesiais e distais em todos os dentes e realizados todos os procedimentos para a confecção das restaurações indiretas. Posteriormente realizou-se a cimentação das restaurações com cimentos resinosos de presa dual. Após esta fase, foram realizados os procedimentos de termociclagem e penetração do corante. Cada dente foi seccionado em cortes de 1,0mm e em seguida, obtida a imagem scaneada de cada corte. Realizou-se a medição linear da infiltração do corante em milímetros por meio de um “software” para este fim. Os resultados foram submetidos à análise pelo teste “t pareado”, adotando nível de significância de 5%. Observou-se, neste estudo, que nenhum dos materiais testados foi capaz de impedir completamente a microinfiltração. O Enforce apresentou os menores valores de infiltração, no entanto não existiram diferenças estatisticamente significantes em relação aos dois materiais estudados.
Título en inglés
In vitro evaluation of marginal leakage of indirect restorations with composed resin in primary molars, cemented with two types of cements
Resumen en inglés
The aim of the present investigation was to evaluate the microleakage of Class II indirect restorations with composed resin Filtek Z250 and cemented with two types of cements: Adhesive Cement Enforce and RelyX Adhesive Resinous Cement. The experimental sample consisted of twenty-four seconds primary molars. Mesiais and distais cavities were prepared in all the teeth and accomplished the procedures to make indirect restorations. After, they were cemented with two types of resinous cements. Soon after that, the specimes were thermocycled, immersed in 0,5% basics fuchsin and sectioned. The microleakage was measured by a software and assessed the dye penetration at the cervical margins. The results were submitted to the analysis by test “t dependet”. The results demonstrated that none of the tested materials was capable to impede the microleakage completely, and there was no significant differences in relation to the two studied materials.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2005-04-04
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.