Doctoral Thesis
DOI
10.11606/T.25.2010.tde-02062011-100708
Document
Author
Full name
Jefferson Tomio Sanada
Institute/School/College
Knowledge Area
Date of Defense
Published
Bauru, 2010
Supervisor
Committee
Valle, Accacio Lins do (President)
Insaurralde, Elizeu
Oliveira, Pedro Cesar Garcia de
Pinto, Joao Henrique Nogueira
Ribeiro, Ricardo Faria
Title in Portuguese
Avaliação da resistência a tração de diferentes enxertos em calvária de ratos
Keywords in Portuguese
Implantes dentários
Materiais biocompatíveis
Osso
Abstract in Portuguese
A perda do osso alveolar como resultado de doença periodontal ou secundariamente à cirurgia são fontes de inúmeras complicações para os cirurgiões dentistas, e a solução para tal problema se baseiam em procedimentos regenerativos, que é realizada através de enxertos ósseos que estabelecem um arcabouço para a reparação tecidual, aumentando os tecidos ósseos nos defeitos resultantes de trauma ou cirurgias, preenchendo os alvéolos após extração para preservar a altura e espessura do rebordo alveolar e aumentando e/ou reconstruindo o rebordo alveolar. Este projeto tem como objetivo determinar a resistência à tração do osso neoformado com a utilização de diferentes biomateriais. Foram utilizados 60 animais divididos em 3 grupos. O grupo 1A (n=10): GenO; Grupo 1B (n=10): GenMix; Grupo1C (n=10): Bio-Oss; Grupo 2a (n=10): PerioGlas; Grupo 2b (n=10): Polímero de mamona e Grupo 3 (n=10): coágulo. Após 3 meses de nascimento os animais foram submetidos a anestesia intraperitonial e confecção de defeito não critico (3mm de diâmetro) na calvária dos animais, que foram preenchidos com os biomateriais correspondentes a cada grupo. Após 6 meses da cirurgia foi realizada a morte dos animais, os espécimes foram coletados e submetidos ao teste em uma máquina de teste universal. Observa-se que o grupo que obteve maior média de resistência à tração foi o grupo de polímero de mamona (10,932±4,529MPa). Consequentemente, obteve-se uma comparação descrescente na seguinte ordem: Coágulo (9,563±3,74MPa), Bio-Oss (8,706±4,087MPa), GenMix (8,587±3,602MPa), GenOx (7,709±2,416MPa), PerioGlas (7,185±6,837MPa), não notando-se diferença estatisticamente significante entre os grupos. Nas microscopias eletrônicas de varredura na maioria dos grupos observou-se presença de fibras colágenas ao redor do tecido ósseo neoformado e dos remanescentes de enxerto. Conclui-se que o material foi indiferente para o resultado final da resistência à tração, demonstrando uma boa qualidade dos materiais utilizados, tanto quando comparamos os produtos quanto a sua origem (xenogênica, polimérica ou coágulo), ou a sua procedência de fabricação (nacional ou importado).
Title in English
Evaluation of the tensile strength of different grafts in rat calvaria
Keywords in English
Biocompatible materials
Bone
Implant
Abstract in English
The loss of alveolar bone as a result of periodontal disease or secondary to surgery are numerous sources of complications for the dentists, and the solution to this problem are based on regenerative procedures, which is conducted through bone grafts that provide a scaffold for tissue repair by increasing the bone tissues in the defects resulting from trauma or surgery, filling the alveoli after extraction to preserve the height and thickness and increasing the alveolar ridge and/or reconstructing the alveolar ridge. This project aims to determine the tensile strength of newly formed bone with the use of different biomaterials. We used 60 animals divided into three groups. Group 1A (n = 10): GenOx; Group 1B (n = 10): GenMix; Group 1C (n = 10): Bio-Oss; Groups 2a (n = 10): PerioGlas; Group 2b (n = 10): castor bean polymer; Group 3 (n = 10): clot. After 3 months of birth the animals were anesthetized intraperitoneally and making non critical defect (3mm diameter) in the calvaria of the animals, which were filled with biomaterials for each group. After 6 months of surgery was performed the animals' death, the specimens were collected and tested in a universal testing machine. It is observed that the group had a higher average tensile strength was the castor oil polymer group (10.932 ± 4.529 MPa). Consequently, we obtained a comparison descended in the following order: Clot (9.563 ± 3.74 MPa), Bio-Oss (8.706 ± 4.087 MPa), GenMix (8.587 ± 3.602 MPa), GenOx (7.709 ± 2.416 MPa), PerioGlas (7.185 ± 6.837 MPa), not noticing a significant difference between the groups. In scanning electron microscopies in most groups there was presence of collagen fibers around the newly formed bone and remaining graft. It is concluded that the material was irrelevant to the final result of the tensile strength, showing a good quality of materials used, both when comparing products as their source (xenogenic, polymeric or clot), or its origin of manufacture (national or imported).
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2011-06-03
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.