• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Doctoral Thesis
DOI
10.11606/T.25.2009.tde-03072009-150523
Document
Author
Full name
Estevam Augusto Bonfante
Institute/School/College
Knowledge Area
Date of Defense
Published
Bauru, 2009
Supervisor
Committee
Pegoraro, Luiz Fernando (President)
Cesar, Paulo Francisco
Correr Sobrinho, Lourenço
Oliveira, Pedro Cesar Garcia de
Silva, Nelson Renato França Alves da
Title in Portuguese
Confiabilidade e modos de fratura de próteses fixas implanto-suportadas metalocerâmicas e em zircônia
Keywords in Portuguese
Cerâmica dentária
Prótese parcial fixa
Zircônia
Abstract in Portuguese
A falha coesiva na porcelana de revestimento de próteses com infraestruturas de policristais de zircônia tetragonal estabilizada por ítrio (PZT-Y) tem causado elevadas taxas clínicas de fracassos. No presente estudo avaliou-se a confiabilidade e modos de fratura de próteses fixas implanto-suportadas confeccionadas em uma liga de Paládio-Prata (PdAg) e em PZT-Y, submetidas à fadiga acelerada progressiva. Embebeu-se análogos de implantes em uma resina acrílica. Infra-estruturas em PZT-Y e PdAg (n = 21/ grupo) foram fabricadas, revestidas com porcelana, cimentadas e submetidas a uma carga estática (n = 3/ grupo) para obtenção dos valores de resistência à fratura. Em seguida, 18 espécimes de cada grupo foram distribuídos ao longo de 3 perfis de estresse progressivo e submetidos à fadiga em água com a carga aplicada na cúspide vestibular do pôntico. Encontrou-se no grupo PdAg um modo de fratura incluindo trincas flexurais na área do conector competindo com a falha coesiva da porcelana, enquanto que as próteses em PZT-Y apresentaram falha coesiva na porcelana de revestimento. O cálculo da confiabilidade (Alta Pro, ReliaSoft, intervalo de confiança de 90 %, bilateral) revelou a ausência de diferença significativa para a finalização de uma missão de 50.000 ciclos a 300 N entre as próteses em PdAg e PZT-Y. Contudo, a confiabilidade reduziu significativamente para o grupo PZT-Y na finalização de uma missão de 100.000 ciclos a 300 N enquanto que permaneceu a mesma para o grupo PdAg. Concluiu-se que para uma missão de 100.000 ciclos a 300 N a confiabilidade é mais alta para a prótese metalocerâmica quando comparada à em PZT-Y. Os modos de fratura diferiram entre os grupos.
Keywords in English

Abstract in English
Statement of problem: chipping within veneering porcelain has resulted in high clinical failure rates for implant-supported zirconia (Y-TZP) bridges. This study evaluated the reliability and failure modes of mouth-motion step-stress fatigued implant-supported Y-TZP versus Palladium-Silver alloy (PdAg) three-unit bridges. Methods: Implant-abutment replicas were embedded in polymethylmethacrylate resin. Y-TZP and PdAg frameworks, of similar design (n=21 each), were fabricated, veneered, cemented (n=3 each), and Hertzian contact tested to obtain ultimate failure load. In each framework group eighteen specimens were distributed across 3 step-stress profiles and mouth-motion cyclically loaded according to the profile on the lingual slope of the buccal cusp of the pontic. Results: PdAg failures included competing flexural cracking at abutment and/or connector area and chipping, whereas Y-TZP presented predominantly cohesive failure within veneering porcelain. Including all failure modes, the reliability (2-sided at 90% confidence intervals) for a mission of 50,000 and 100,000 cycles at 300 N load was determined (Alta Pro, Reliasoft). No difference in reliability was observed between groups for a mission of 50,000. Reliability remained unchanged for a mission of 100,000 for PdAg, but significantly decreased for Y-TZP. Conclusion: Higher reliability was found for PdAg for a mission of 100,000 cycles at 300N. Failure modes differed between materials.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2009-07-03
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.