Tesis Doctoral
DOI
10.11606/T.25.2009.tde-03072009-150523
Documento
Autor
Nombre completo
Estevam Augusto Bonfante
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2009
Director
Tribunal
Pegoraro, Luiz Fernando (Presidente)
Cesar, Paulo Francisco
Correr Sobrinho, Lourenço
Oliveira, Pedro Cesar Garcia de
Silva, Nelson Renato França Alves da
Título en portugués
Confiabilidade e modos de fratura de próteses fixas implanto-suportadas metalocerâmicas e em zircônia
Palabras clave en portugués
Cerâmica dentária
Prótese parcial fixa
Zircônia
Resumen en portugués
A falha coesiva na porcelana de revestimento de próteses com infraestruturas de policristais de zircônia tetragonal estabilizada por ítrio (PZT-Y) tem causado elevadas taxas clínicas de fracassos. No presente estudo avaliou-se a confiabilidade e modos de fratura de próteses fixas implanto-suportadas confeccionadas em uma liga de Paládio-Prata (PdAg) e em PZT-Y, submetidas à fadiga acelerada progressiva. Embebeu-se análogos de implantes em uma resina acrílica. Infra-estruturas em PZT-Y e PdAg (n = 21/ grupo) foram fabricadas, revestidas com porcelana, cimentadas e submetidas a uma carga estática (n = 3/ grupo) para obtenção dos valores de resistência à fratura. Em seguida, 18 espécimes de cada grupo foram distribuídos ao longo de 3 perfis de estresse progressivo e submetidos à fadiga em água com a carga aplicada na cúspide vestibular do pôntico. Encontrou-se no grupo PdAg um modo de fratura incluindo trincas flexurais na área do conector competindo com a falha coesiva da porcelana, enquanto que as próteses em PZT-Y apresentaram falha coesiva na porcelana de revestimento. O cálculo da confiabilidade (Alta Pro, ReliaSoft, intervalo de confiança de 90 %, bilateral) revelou a ausência de diferença significativa para a finalização de uma missão de 50.000 ciclos a 300 N entre as próteses em PdAg e PZT-Y. Contudo, a confiabilidade reduziu significativamente para o grupo PZT-Y na finalização de uma missão de 100.000 ciclos a 300 N enquanto que permaneceu a mesma para o grupo PdAg. Concluiu-se que para uma missão de 100.000 ciclos a 300 N a confiabilidade é mais alta para a prótese metalocerâmica quando comparada à em PZT-Y. Os modos de fratura diferiram entre os grupos.
Palabras clave en inglés

Resumen en inglés
Statement of problem: chipping within veneering porcelain has resulted in high clinical failure rates for implant-supported zirconia (Y-TZP) bridges. This study evaluated the reliability and failure modes of mouth-motion step-stress fatigued implant-supported Y-TZP versus Palladium-Silver alloy (PdAg) three-unit bridges. Methods: Implant-abutment replicas were embedded in polymethylmethacrylate resin. Y-TZP and PdAg frameworks, of similar design (n=21 each), were fabricated, veneered, cemented (n=3 each), and Hertzian contact tested to obtain ultimate failure load. In each framework group eighteen specimens were distributed across 3 step-stress profiles and mouth-motion cyclically loaded according to the profile on the lingual slope of the buccal cusp of the pontic. Results: PdAg failures included competing flexural cracking at abutment and/or connector area and chipping, whereas Y-TZP presented predominantly cohesive failure within veneering porcelain. Including all failure modes, the reliability (2-sided at 90% confidence intervals) for a mission of 50,000 and 100,000 cycles at 300 N load was determined (Alta Pro, Reliasoft). No difference in reliability was observed between groups for a mission of 50,000. Reliability remained unchanged for a mission of 100,000 for PdAg, but significantly decreased for Y-TZP. Conclusion: Higher reliability was found for PdAg for a mission of 100,000 cycles at 300N. Failure modes differed between materials.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-07-03
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.