Disertación de Maestría
DOI
10.11606/D.25.2005.tde-11042015-110150
Documento
Autor
Nombre completo
Thania Grisel Rodriguez Almonte
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2005
Director
Tribunal
Ferreira, Paulo Martins (Presidente)
Francisconi, Paulo Afonso Silveira
Segalla, Jose Claudio Martins
Título en portugués
Avaliação da resistência à fratura de prótese parcial fixa provisória confeccionada sobre componentes do tipo UCLA em titânio - efeito de diversos reforços
Palabras clave en portugués
Fibras de vidro
Kevlar
Poli(metilmetacrilato)
Próteses fixas sobre implantes
Próteses reforçadas
Reforços metálicos
Resinas acrílicas
Teste de materiais próteses provisória
Resumen en portugués
As restaurações provisórias no tratamento reabilitador oral são de suma importância. Por isso é preocupante que os materiais utilizados para a execução das mesmas sejam críticos com relação à sua resistência e longevidade, principalmente, quando estas são executadas em tratamentos prolongados e/ou em espaços desdentados extensos. O objetivo deste trabalho foi avaliar em 4 grupos reforçados, compostos por 9 espécimes cada um, a resistência e o modo de fratura, de uma resina acrílica poli(metilmetacrilato) auto-polimerizável (Dencor® - Clássico®, São Paulo, SP, Brasil) utilizada para restaurações provisórias quando reforçada com fibras de vidro (Fibrante® e Interlig® - Angelus®, Londrina, PR, Brasil), fibras de aramida (Kevlar® - Du Pont®, USA) y fio ortodôntico ∅ 0, 7mm. E um grupo controle sem nenhum tipo de reforço, com a mesma quantidade de corpos de prova. A análise dos resultados (ANOVA, p < 0,05), para o teste de resistência, mostrou haver diferença estatística entre os grupos. O teste de Tukey encontrou que os grupos reforçados, aqueles que alcançaram maior média de resistência à fratura foram os que utilizaram a fibra de vidro trançada pré-impregnada com resina composta foto-polimerizável, Interlig® (1083 N); a fibra de vidro unidirecional préimpregnada com dimetacrilato de glicol, Fibrante® (1022 N) e a fibra de poli(aramida) unidirecional sem pré-impregnação, Kevlar® 29, aumentando em 26%, 22% e 17%, respectivamente, esta resistência em relação ao grupo controle (800 N), não havendo diferença estatística significante entre eles. O grupo reforçado com fio de aço com ∅ 0,7 mm (871 N) apareceu em seguida com uma resistência somente 8% maior e semelhante àquela apresentada pelo grupo controle sem reforço. A análise das fraturas concorreu com a elaboração de um novo sistema de classificação dividindo-as em quatro tipos: Ausente, Parcial, Total Não Separada e Total Separada. As fraturas dos espécimes reforçados foram consideradas mais favoráveis ocorrendo, predominantemente, os tipos Ausente e Parcial.
Título en inglés
Fracture resistance evaluation of provisional fixed partial denture made on titanium ucla components several reinforcements effect
Palabras clave en inglés
Acrylic resins
Fixed prosthesis on implants
Glass fiber
Kevlar reinforced prostheses
Metal reinforcements
Poly (methylmethacrylate)
Provisional prosthetic materials test
Resumen en inglés
Provisional restorations are of ultimate importance in the oral rehabilitation treatment. Thus, clinicians have to bear in mind that materials used for their fabrication are critical due to its longevity and strength, when these are done for longterm therapy and/or large edentulous spaces. The aim of this work was to evaluate the flexural resistance and fracture mode of an auto-cure polymethylmetacrilate resin (Dencor® - Classico® , Sao Paulo, SP, Brasil) used for provisional restorations and reinforced with four materials. Samples were divided in four groups of nine each, as the following: glass fiber (Fibrante® and Interlig® Angelus®, Londrina, PR, Brasil), aramide fibers (Kevlar® Du Pont®, USA), and orthodontic wire ∅ 0,7mm. one group whitout reinforcement served as control. Data was submitted to statistical analysis with one-way ANOVA (p<.05) test. Results showed statistically significant difference among the groups. Tukeys test showed that glass-fiber Interlig® exhibited the greatest value of flexural strength (1083 N); followed by unidirectional glycol dimetacrylate glass-fiber Fibrante® (1022 N) and aramid fiber Kevlar® (966 N). These values represent 26%, 22% and 17% in relation to the control group (800 N), being non statistically significant difference observed among them. The group with ∅ 0,7mm orthodontic wire (871 N) had a resistance only 8% higher and similar of that of control group without reinforcement. Fracture analysis was conducted by the following scale: absence, partial, complete without separation, and complete with separation. Fracture modes observed on reinforced samples were considered more favorable, with types absent and partial seeing more frequently.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-04-15
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.