Mémoire de Maîtrise
DOI
10.11606/D.25.2005.tde-11042015-110150
Document
Auteur
Nom complet
Thania Grisel Rodriguez Almonte
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Bauru, 2005
Directeur
Jury
Ferreira, Paulo Martins (Président)
Francisconi, Paulo Afonso Silveira
Segalla, Jose Claudio Martins
Titre en portugais
Avaliação da resistência à fratura de prótese parcial fixa provisória confeccionada sobre componentes do tipo UCLA em titânio - efeito de diversos reforços
Mots-clés en portugais
Fibras de vidro
Kevlar
Poli(metilmetacrilato)
Próteses fixas sobre implantes
Próteses reforçadas
Reforços metálicos
Resinas acrílicas
Teste de materiais próteses provisória
Resumé en portugais
As restaurações provisórias no tratamento reabilitador oral são de suma importância. Por isso é preocupante que os materiais utilizados para a execução das mesmas sejam críticos com relação à sua resistência e longevidade, principalmente, quando estas são executadas em tratamentos prolongados e/ou em espaços desdentados extensos. O objetivo deste trabalho foi avaliar em 4 grupos reforçados, compostos por 9 espécimes cada um, a resistência e o modo de fratura, de uma resina acrílica poli(metilmetacrilato) auto-polimerizável (Dencor® - Clássico®, São Paulo, SP, Brasil) utilizada para restaurações provisórias quando reforçada com fibras de vidro (Fibrante® e Interlig® - Angelus®, Londrina, PR, Brasil), fibras de aramida (Kevlar® - Du Pont®, USA) y fio ortodôntico ∅ 0, 7mm. E um grupo controle sem nenhum tipo de reforço, com a mesma quantidade de corpos de prova. A análise dos resultados (ANOVA, p < 0,05), para o teste de resistência, mostrou haver diferença estatística entre os grupos. O teste de Tukey encontrou que os grupos reforçados, aqueles que alcançaram maior média de resistência à fratura foram os que utilizaram a fibra de vidro trançada pré-impregnada com resina composta foto-polimerizável, Interlig® (1083 N); a fibra de vidro unidirecional préimpregnada com dimetacrilato de glicol, Fibrante® (1022 N) e a fibra de poli(aramida) unidirecional sem pré-impregnação, Kevlar® 29, aumentando em 26%, 22% e 17%, respectivamente, esta resistência em relação ao grupo controle (800 N), não havendo diferença estatística significante entre eles. O grupo reforçado com fio de aço com ∅ 0,7 mm (871 N) apareceu em seguida com uma resistência somente 8% maior e semelhante àquela apresentada pelo grupo controle sem reforço. A análise das fraturas concorreu com a elaboração de um novo sistema de classificação dividindo-as em quatro tipos: Ausente, Parcial, Total Não Separada e Total Separada. As fraturas dos espécimes reforçados foram consideradas mais favoráveis ocorrendo, predominantemente, os tipos Ausente e Parcial.
Titre en anglais
Fracture resistance evaluation of provisional fixed partial denture made on titanium ucla components several reinforcements effect
Mots-clés en anglais
Acrylic resins
Fixed prosthesis on implants
Glass fiber
Kevlar reinforced prostheses
Metal reinforcements
Poly (methylmethacrylate)
Provisional prosthetic materials test
Resumé en anglais
Provisional restorations are of ultimate importance in the oral rehabilitation treatment. Thus, clinicians have to bear in mind that materials used for their fabrication are critical due to its longevity and strength, when these are done for longterm therapy and/or large edentulous spaces. The aim of this work was to evaluate the flexural resistance and fracture mode of an auto-cure polymethylmetacrilate resin (Dencor® - Classico® , Sao Paulo, SP, Brasil) used for provisional restorations and reinforced with four materials. Samples were divided in four groups of nine each, as the following: glass fiber (Fibrante® and Interlig® Angelus®, Londrina, PR, Brasil), aramide fibers (Kevlar® Du Pont®, USA), and orthodontic wire ∅ 0,7mm. one group whitout reinforcement served as control. Data was submitted to statistical analysis with one-way ANOVA (p<.05) test. Results showed statistically significant difference among the groups. Tukeys test showed that glass-fiber Interlig® exhibited the greatest value of flexural strength (1083 N); followed by unidirectional glycol dimetacrylate glass-fiber Fibrante® (1022 N) and aramid fiber Kevlar® (966 N). These values represent 26%, 22% and 17% in relation to the control group (800 N), being non statistically significant difference observed among them. The group with ∅ 0,7mm orthodontic wire (871 N) had a resistance only 8% higher and similar of that of control group without reinforcement. Fracture analysis was conducted by the following scale: absence, partial, complete without separation, and complete with separation. Fracture modes observed on reinforced samples were considered more favorable, with types absent and partial seeing more frequently.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2015-04-15
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.