Disertación de Maestría
DOI
10.11606/D.25.2009.tde-29052009-101406
Documento
Autor
Nombre completo
Marcus Gustavo Silva Rodrigues
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2009
Director
Tribunal
Rezende, Maria Lucia Rubo de (Presidente)
Romito, Giuseppe Alexandre
Sant'Ana, Adriana Campos Passanezi
Título en portugués
Efeito da desmineralização das superfícies de contato na resistência à tração de enxertos ósseos autógenos em tíbia de coelhos. Analise mecânica e à microscopia eletrônica de varredura
Palabras clave en portugués
Desmineralização
Osseointegração
Transplante ósseo
Resumen en portugués
Vinte e nove coelhos machos (Oryctolagus cuniculus) tiveram fragmentos ósseos corticais de 8mm de diâmetro removidos com trefina da metáfise proximal tibial que foram transplantados para uma área adjacente após a realização de um dos seguintes tratamentos: G-EDTA (desmineralização com EDTA pH neutro a 24% na forma de gel por 3 minutos das superfícies ósseas de contato); G-EDTA-P (o mesmo tratamento de G-EDTA e perfuração do leito receptor); G-P (perfuração do leito receptor) e G-C (nenhum tratamento adicional ao transplante). Noventa dias após as cirurgias, os animais foram eutanasiados para obtenção de blocos ósseos contendo os enxertos e preparo de corpos de prova para ensaio mecânico de determinação da resistência à tração e módulo de elasticidade. Os valores encontrados para resistência à tração foram: G-C = 2.0861.200 MPa; G-EDTA = 2.0330.976 MPa; G-EDTA-P = 1.9770.795 MPa e G-P = 1.8260.800 MPa. Entretanto, não houve diferença estatisticamente significante entre os grupos (p=0.819). Os valores médios do módulo de elasticidade foram: G-C = 38.8022.72 MPa; G-EDTA-P = 26.2414.17 MPa; G-EDTA = 25.119.89 MPa e G-P = 17.517.94 MPa, sendo identificada diferença estatística apenas entre o G-C e os demais. Concluiu-se que a desmineralização por EDTA das superfícies ósseas de contato em enxertos autógenos em bloco do tipo onlay não interfere na resistência à tração da interface independentemente da perfuração do leito receptor e que tanto a desmineralização como a perfuração aumentam a deformação dos corpos de prova sugerindo um melhor comportamento elástico nesses grupos.
Título en inglés
Effect of the demineralization of the contacting surfaces in the tensile strength of autogenous bone grafts in rabbits tibiae. Mechanical and scanning electron microscopy analysis
Palabras clave en inglés
Bone transplantation
Demineralization
Osseointegration
Resumen en inglés
Cortical bone fragments of 8mm of diameter were removed with trephine burr from the proximal tibial metaphysis of twenty nine male rabbits (Oryctolagus cuniculus) and transplanted to an adjacent area after one of the following treatments: G-EDTA (demineralization of the contacting bone surfaces with EDTA pH 24% during 3 minutes); G-EDTA-P (the same treatment of G-EDTA and perforation of the receiving host bed); G-P (perforation of the receiving host bed) and G-C (no additional treatment to the transplant). Ninety days post-operatively, the animals were euthanized in order to attain bone blocks with the grafts. The specimens were prepared to mechanical assay for tensile strength and Young modulus. The values found for tensile strenght were: G-C = 2.086±1.200 MPa; G-EDTA = 2.033±0.976 MPa; G-EDTA-P = 1.977±0.795 MPa and G-P = 1.826±0.800 MPa. These differences, therefore, were not statically significant (p=0.819). The Young modulus average values for the specimens were: G-C = 38.80±22.72 MPa; G-EDTA-P = 26.24±14.17 MPa; G-EDTA = 25.11±9.89 MPa and G-P = 17.51±7.94 MPa. There were statistically significant differences only between the G-C and the other groups. The results showed that EDTA demineralization of the contacting bone surfaces in onlay autogenous bone grafts does not interfere in the tensile strenght at the interface independently of the perforation of the host bed. On the other hand, demineralization as well as perforation increased the deformation of the specimens suggesting a better elastic behavior for these groups.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-06-02
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.