Tesis Doctoral
DOI
10.11606/T.25.2016.tde-07112016-162728
Documento
Autor
Nombre completo
Fernanda Ferruzzi Lima
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2016
Director
Tribunal
Rubo, Jose Henrique (Presidente)
Bonfante, Estevam Augusto
Borges, Ana Flávia Sanches
Cesar, Paulo Francisco
Sábio, Sérgio
Título en portugués
Avaliação da resistência à fadiga e modalidades de danos de coroas unitárias de dissilicato de lítio e resina nanocerâmica
Palabras clave en portugués
Cerâmicas
Coroas dentárias
Fadiga
Polímeros
Projeto auxiliado por computador
Resumen en portugués
Fraturas completas ou por delaminação são causas frequentes de insucesso entre coroas unitárias cerâmicas. O uso de materiais à base de resina composta, em contraponto à natureza friável das cerâmicas, parece ser uma alternativa para coroas posteriores, uma vez que apresentam processo de fabricação e reparo simplificados. Este estudo avalia a resistência à fadiga de coroas unitárias monolíticas CAD/CAM de resina composta nanocerâmica e cerâmica reforçada por dissilicato de lítio, bem como os danos causados pela aplicação de carga cíclica. Vinte e seis coroas monolíticas (n=13) foram cimentadas sobre réplicas de resina composta de um molar preparado e submetidas à ciclagem mecânica durante 2 milhões de ciclos, sob carga máxima de 350N à frequência de 2 Hz. Não foram observadas fraturas catastróficas ou fratura coesiva das coroas, resultando em sobrevivência de 100% para os dois materiais avaliados. As coroas foram incluídas em resina epóxi e desgastadas progressivamente à procura de danos. Coroas em resina nanocerâmica apresentaram-se íntegras, com trincas do cone externo, trincas do cone interno e com trincas radiais. As coroas em dissilicato de lítio apresentaram trincas do cone externo e interno, algumas atingindo a superfície interna. Os danos receberam escores de acordo com a severidade. Os dados foram submetidos à análise estatística pelo teste de Mann-Whitney (p =0,462), que não revelou diferenças estatísticas em relação aos danos observados. Concluímos que coroas monolíticas em dissilicato de lítio e resina nanocerâmica podem ser utilizadas na região posterior, pois apresentaram resistência à fadiga equivalente, sem diferença estatística entre os danos apresentados.
Título en inglés
Evaluation of the fatigue resistance and damage modes of lithuim disilicate and resin nanoceramic
Palabras clave en inglés
Ceramics
Computer aided design
Dental crowns
Fatigue
Polymers
Resumen en inglés
Bulk fractures or cohesive fractures are frequent complications for ceramic crowns. The use of resin- based materials, in contrast to the brittle nature of ceramics, seems to be an alternative to posterior crowns, since these materials present simplified manufacturing and repair tehniques. This study evaluates the fatigue resistance of monolithic CAD / CAM crowns made of resin nanoceramic and lithium disilicate reinforced ceramic, as well as the damage modes caused by the application of cyclic loading. Twenty-six monolithic crowns (n = 13) were cemented to a composite resin replica of a prepared molar and subjected to cyclic load over 2 million cycles under maximum load of 350N, at a frequency of 2 Hz. The crowns presented no catastrophic failures or cohesive fractures, resulting in survival of 100% for both materials. The crowns were embedded in epoxy resin and gradually grinded for damage analisys. Nanoceramic resin crowns presented no damage, outer cone cracks, inner cone cracks and radial cracks. Lithium disilicate crowns showed outer and inner cone cracks, some of the latter reaching the inner surface. Specimens were scored according to the severity of damage. Data was subjected to Mann-Whitney test (p = 0.462), which revealed no statistical difference. We conclude that lithium disilicate and resin nanoceramic monolithic crowns can be used in the posterior area, since they presented comparable fatigue resistance, with no statistical difference between damage modes.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-11-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.