Disertación de Maestría
DOI
10.11606/D.25.2015.tde-03092015-092531
Documento
Autor
Nombre completo
Luara Aline Pires
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2015
Director
Tribunal
Borges, Ana Flávia Sanches (Presidente)
Fortulan, Carlos Alberto
Oliveira, Rodrigo Cardoso de
Título en portugués
Resposta in vitro de células pré-osteoblásticas em cerâmica de hidroxiapatita
Palabras clave en portugués
Durapatita
Materiais biocompatíveis
Sobrevivência celular
Resumen en portugués
Com a evolução do Biomateriais houve melhorias nas opções de tratamentos e atualmente são utilizados em substituição de partes do corpo que foram perdidas e promovem a recuperação de funções biológicas. Dentre eles existem as chamadas Biocerâmicas, que incluem alumina, zircônia e derivadas de fosfato de cálcio. A hidroxiapatita possui composição e estrutura minerais semelhantes à fase mineral óssea e apresenta como propriedades a biocompatibilidade, osteocondutividade e bioatividade. O trabalho avaliou a viabilidade celular em cerâmica de hidroxiapatita experimental de origem bovina em comparação com dois tipos de zircônia comerciais e liga de titânio comercialmente puro, para que futuramente possa ser utilizada como material base para implantes dentários. A avaliação in vitro foi realizada por meio de testes nos quais células pré-osteoblásticas cultivadas de linhagem murina MC3T3-E1 foram colocadas em contato indireto e direto com estes materiais. Para viabilidade celular (n=8) foram feitos testes de ensaio MTT e Cristal Violeta em duplicata e após 24, 48 e 72 horas os níveis de absorbâncias foram analisados por meio de espectrofotometria no leitor de Elisa. Para as analises por microscopia eletrônica de varredura (n=6) as células foram plaqueadas diretamente sobre as superfícies dos discos, fixadas em vapor de tetróxido de ósmio 2% após 24 e 48 horas, seguido da metalização após 48 horas da fixação das células para análise em Microscópio Eletrônico de Varredura. Os resultados para viabilidade indireta foram submetidos ao teste paramétrico ANOVA, seguido de teste de Tukey (p<0,05). Tanto no teste de MTT quanto no Cristal Violeta, de acordo com o grupo controle positivo, todos os grupos apresentaram resultados satisfatórios. A cerâmica de hidroxiapatita não apresentou diferença estatística significante, demonstrando não ser um material citotóxico. Pelas imagens geradas no MEV do teste de viabilidade direta, verificou-se que houve adesão e proliferação das células nos dois períodos sobre as superfícies dos materiais. Portanto, pode-se afirmar que a cerâmica de hidroxiapatita apresentou-se como um material biocompatível.
Título en inglés
Palabras clave en inglés
Biocompatible materials
Cell survival
Durapatite
Resumen en inglés
With the evolution biomaterials there were improvements in treatment options, and are currently used in replacement body parts that were lost and promote the recovery of biological functions. Among them are the bioceramic which include alumina, zirconia and calcium phosphate derivative. Hydroxyapatite has mineral composition and structure similar to bone mineral phase and can be used as a biomaterial having biocompatibility, osteoconductivity and bioactivity. The study evaluated the cell viability in experimental hydroxyapatite ceramic bovine compared the two types of commercial zirconia and titanium alloy commercially pure, so that in future it can be used as base material for dental implants. In vitro evaluation was carried by means of tests in which the pre-osteoblastic cells MC3T3-E1 murine lineage cultured were placed in indirect and direct contact with these materials. For cell viability (n=8) were carried MTT assay and Crystal Violet tests in duplicate and after 24, 48 and 72 hours the absorbance levels were analyzed by spectrophotometry Elisa reader. For analysis by Scanning Electron Microscope variable pressure (n = 6) cells were plated directly on the discs surfaces, fixed in osmium tetroxide steam 2% after 24 and 48 hours, followed by metallization after 48 of cells fixation. The results for the cell viability were submitted to parametric test ANOVA, followed by Tukey test (p<0.05). Both in the MTT assay as Crystal Violet all groups exhibited satisfactory results absent cytotoxicity. By means of the SEM images produced, it was found that there was adhesion and proliferation of cells on the materials surfaces in the two periods. Therefore, it can be stated that the hydroxyapatite ceramic was presented as a biocompatible material.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-09-04
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.