Disertación de Maestría
DOI
10.11606/D.25.2011.tde-27092011-102146
Documento
Autor
Nombre completo
Maria Cristina Carvalho de Almendra Freitas
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2011
Director
Tribunal
Navarro, Maria Fidela de Lima (Presidente)
Atta, Maria Teresa
Fagundes, Ticiane Cestari
Título en portugués
Avaliação de cimentos de ionômero de vidro modificados por resina frente à incorporação de nanopartículas de vitrocerâmica bioativa
Palabras clave en portugués
Cimentos de ionômero de vidro
Resistência à compressão
Rugosidade
Vitrocerâmica bioativa
Resumen en portugués
Os materiais bioativos são materiais sintéticos que possuem superfícies ativas em que os minerais presentes em tecidos duros podem se ligar quimicamente. Há alguns estudos em Odontologia, onde partículas desses materiais foram incorporadas aos Cimentos de Ionômero de Vidro (CIVs) e Cimentos de Ionômero de Vidro modificados por resina (CIVMRs) com o objetivo de se obter bioatividade, e conseqüente remineralização dentária. O presente estudo teve como objetivo avaliar os efeitos da incorporação de nanopartículas de vitrocerâmica bioativa nas propriedades de resistência à compressão e rugosidade de CIVMRs. Fuji II LC e Vitremer foram considerados os grupos controles. Materiais experimentais foram feitos através da incorporação de 2, 5 e 10% em peso de Biosilicato nestes CIVMRs. Seis corpos-de-prova de cada material foram confeccionados para o teste de resistência à compressão, que foi realizado em máquina de ensaios universal (Emic), a uma velocidade de 1,0 mm/min, depois de mantidos por 24 horas em água destilada a 37°C. Para análise da rugosidade, foram confeccionados dois corpos-de-prova de cada material, armazenados em água destilada por sete dias, para terem suas superfícies analisadas por meio de Microscopia de Força Atômica. Os dados da resistência à compressão e rugosidade foram submetidos à análise estatística por meio da Análise de Variância (ANOVA) a dois critérios e para comparações múltiplas foi aplicado o teste de Tukey, com nível de significância de 5%. Apenas os cimentos com 2% de nanopartículas de vitrocerâmica bioativa obtiveram resistência à compressão semelhante ao grupo controle, as demais concentrações contribuíram para a diminuição dessa resistência. A incorporação de 5% de nanopartículas de vitrocerâmica bioativa aumentou a rugosidade superficial dos CIVMRs estudados.
Título en inglés
Resin modified glass ionomer cements evaluation with additional bioactive glass-ceramics nanoparticles
Palabras clave en inglés
Bioactive glass-ceramic
Compressive strength
Glass-ionomer cements
Roughness
Resumen en inglés
Bioactive materials are synthetic materials that have active surfaces that are capable to chemically bond to dental structures. There are some studies where particles of these materials were incorporated in Glass-ionomer cements (GIC) and Resin-modified glass-ionomer cements (RMGIC) trying to achieve bioactivity and dental remineralization. The aim of this study was to evaluate the effects of the incorporation of bioactive glass-ceramics nanoparticles on the compressive strength and roughness of RMGIC. Fuji II LC and Vitremer were considered the control groups. Experimental materials were made adding 2, 5 and 10% (weight) of Biosilicate into these RMGIC. Six specimens of each material were made to be tested on compressive strength performed with a universal testing machine (Emic) at a crosshead speed of 1.0 mm / min, after they were stored in distilled water for 24 hour at 37°C. To roughness analysis, two specimens of each material were made and stored in distilled water for 7 days and their surfaces were analyzed with a Atomic Force Microscope. Data of compressive strength and roughness were statistically analyzed by ANOVA and Tukey test for multiple comparisons. Only the RMGICs with 2% of bioactive glass-ceramic nanoparticles obtained compressive strength similar to the control RMGICs, the other concentrations decreased their compressive strength values. The incorporation of 5% of bioactive glass-ceramic nanoparticles increased the roughness of the RMGICs.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2011-10-03
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.