Tesis Doctoral
DOI
https://doi.org/10.11606/T.25.2016.tde-25112016-111821
Documento
Autor
Nombre completo
Ricardo Vinicius Nunes Arantes
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Bauru, 2016
Director
Tribunal
Taga, Rumio (Presidente)
Cestari, Tânia Mary
Ribeiro, Andreia Espíndola Vieira
Silveira, Elcia Maria Varize
Yaedú, Renato Yassutaka Faria
Título en portugués
Avaliação microtomográfica e histomorfométrica do processo de reparo de defeitos ósseos em calvária de coelhos tratados com diferentes materiais de enxerto
Palabras clave en portugués
Biomaterial
Cerâmica bifásica de Cálcio
Hidroxiapatita
Resumen en portugués
Um dos grandes desafios para o tratamento de defeitos ósseos extensos na região bucomaxilofacial têm sido o desenvolvimento de um biomaterial substituto ósseo ao enxerto autógeno. No presente trabalho avaliou-se a formação óssea e a biodegrabilidade do osso desproteinizado bovino Bio-Oss® e do seu similar GenOx Inorg® e da cerâmica bifásica GenPhos® XP no processo de reparo de defeitos ósseos cranianos em coelhos, comparativamente ao osso autógeno (controle positivo) e coágulo sanguíneo (controle negativo). Foram realizados cirurgicamente defeitos bilaterais de 8-mm de diâmetro nos ossos parietais de 39 coelhos. A seguir os defeitos foram preenchidos aleatoriamente com 0,1cm3 de material ou coágulo conforme cada grupo de tratamento. Após os períodos de 4, 8 e 24 semanas os crânios foram coletados, analisados no microtomógrafo e processados histologicamente. O percentual de volume do defeito ocupado pelo material e osso neoformado foi avaliado pela microtomografia e histomorfometria, enquanto que, para a medula óssea, tegumento e tecido conjuntivo, apenas pela análise histomorfométrica. Os resultados quantitativos obtidos foram comparados estatisticamente pela ANOVA a dois critérios (período e tratamento) e teste de Tukey com p<0,05. A intensidade da associação linear dos dados microtomográficos e histomorfométricos avaliada pelo coeficiente de correlação de Pearson, mostraram correlação moderada a forte. Nos períodos iniciais de reparo (30 e 60 dias), os defeitos tratados com Bio-Oss®, GenOx® Inorg e GenPhos® XP apresentaram manutenção do volume do material enxertado (Vvi médio de 34% ) e formação óssea menor e mais imatura em relação grupo autógeno (Vvi = 22% vs. 32% no grupo autógeno). No período mais tardio (180 dias) a quantidade de formação óssea foi estatisticamente similar nos grupos Bio-Oss® (Vvi = 27%), GenOx® Inorg (Vvi = 26%) e GenPhos® XP (Vvi = 20%) porém, o GenOx® Inorg promoveu a formação de um tecido ósseo mais organizado e com maior acúmulo de biomaterial+osso+medula óssea (Vvi = 67,9%) comparado ao GenPhos® XP (Vvi =58,9%) e Bio Oss (Vvi = 55,6%) mas, inferior ao do enxerto autógeno (Vvi = 78%). Os resultados aqui obtidos permitem concluir que o osso autógeno promove rápida formação e maturação óssea, porém não consegue promover o reestabelecimento completo da díploe removida cirurgicamente. Os materiais BioOss, GenOx® Inorg e GenPhos® XP são excelentes materiais osteocondutores levando a formação óssea em toda extensão do defeito, sendo o GenOx® Inorg o que apresenta menor grau de reabsorção e maior e melhor preenchimento do defeito.
Título en inglés
Microtomographic and histomorphometric evaluation of bone repair in rabbit cranial defects treated with different graft materials
Palabras clave en inglés
Biomaterial
Biphasic calcium phosphate
Hydroxyapatite
Resumen en inglés
One major challenge for treatment of critical size defects in maxillofacial region has been the development of a substitute biomaterial to the autogenous bone grafts. In present study we evaluated the bone formation and biodegradability of deproteinized bovine bone Bio-Oss® and GenOx® Inorg, and biphasic calcium phosphate GenPhos XP® during bone repair process in rabbits cranial defects compared to autogenous bone (positive control) and blood clot (negative control). In parietal bone of 39 rabbits were made bilateral 8-mm diameter defects, which were filled randomly with 0,1cm3 material or clot as each treatment group. After periods of 4, 8 and 24 weeks skulls of animals were collected, analyzed the MicroCT scanner and histologically processed. The percentage of defect volume occupied by biomaterial and new-formed bone were assessed by histomorphometry and microtomography, while the bone marrow, connective tissue and tegument only by first analysis. The quantitative data were compared by two-way ANOVA analysis (time and treatment) and Tukey's test at p <0.05. The intensity of the linear association of MicroCT and morphometric data evaluated by the Pearson correlation coefficient, showed moderate to strong correlation. In the early repair periods (30 and 60 days), the defects treated with Bio- Oss, GenOx® Inorg and GenPhos® XP showed maintenance of the graft material volume (average Vvi of 34%) and lower and more immature bone compared autograft group (Vvi = 22% vs. 32% in the autograft group). In the later period (180 days) the amount of bone formation was statistically similar to the groups Bio-Oss® (Vvi = 27 %), GenOx® Inorg (Vvi = 26%) and GenPhos® XP (Vvi = 20%) however, the bone formation in GenOx® Inorg was more organized and with greater accumulation of particles + bone tissue + bone marrow (Vvi = 67.9%), when compared to GenPhos® XP (Vvi = 58.9%) and Bio-Oss® (Vvi = 55.6%) but lower than the autograft (Vvi = 78%). It was concluded that the autogenous bone promotes rapid bone formation and maturation, but cannot promote the complete reestablishment of diploe surgically removed. The Bio-Oss®, GenOx® Inorg and GenPhos® XP are excellent osteoconductive materials leading to bone formation in the full extent of the defects, and the GenOx® Inorg showing less absorption promotes more and better defect filling.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-12-05
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.