Disertación de Maestría
DOI
10.11606/D.3.2017.tde-02032017-144335
Documento
Autor
Nombre completo
Ana Paula Gonçalves Chaves
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2016
Director
Tribunal
Goldenstein, Helio (Presidente)
Franco, Luiz Alberto Pereira das Neves
Alves, Luiz Henrique Dias
Título en portugués
Rodas ferroviárias: análise, microestrutura e propostas de melhoria.
Palabras clave en portugués
Aço
Desgaste
Distância interlamelar da perlita
Ferrovias
Mudança de fase
Rodas
Trilhos
Resumen en portugués
A pesquisa relativa ao transporte ferroviário no Brasil tem se intensificado nos últimos anos visando principalmente a melhoria no desempenho do par rodatrilho. Isso se deve à demanda de se transportar cada vez mais carga por eixo com a finalidade de reduzir o custo de transporte. Através de mudanças na microestrutura do material ou de mudanças na composição das ligas utilizadas na fabricação pode se aumentar a resistência do par roda-trilho. Neste trabalho foi analisada a influência de diferentes microestruturas (puramente perlíticas e perlíticas-bainíticas), obtidas por meio de tratamento térmico por dilatometria, nas propriedades de um aço alto carbono similar ao utilizado em rodas convencionais classe C AAR destinadas ao transporte de carga pesada. As análises empregaram técnicas metalográficas (identificação de fases presentes e distância interlamelar da perlita), ensaios magnéticos (saturação magnética e ruído magnético de Barkhausen), ensaio mecânico de dureza e ensaio tribológico de resistência ao desgaste por deslizamento. Foram caracterizadas rodas ferroviárias classe C AAR em quatro condições distintas: usadas e novas, fundidas e forjadas.
Título en inglés
Railway wheels: analysis, microstructure and improvement proposals.
Palabras clave en inglés
Pearlite interlamellar spacing
Railway wheels
Sliding wear
Resumen en inglés
Research about rail transport in Brazil has been intensified recently due the need to improve the wheel-rail performance, considering the demand of increasing axle load aiming for transportation cost reduction. Changes in the material microstructure or in the alloys composition can improve the wheel-rail resistance. A eutectoid steel similar to that used in conventional class C AAR wheels (designed to heavy haul transportation - high loads and low speeds) was submitted to isothermal heat treatments applying dilatometry techniques at ten different cycles. Different microstructures (totally pearlitic and pearlitic-bainitic) were obtained and their influence on the mechanical and magnetic properties was analyzed. The analysis included metallographic techniques (identification of phases and pearlite interlamellar spacing), magnetic testing (magnetic saturation and magnetic Barkhausen noise) and mechanical testing (hardness and pin-ondisc tests). Railway wheels Class C ARR were characterized in four different conditions: new and used, cast and forged.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-03-06
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.