Mémoire de Maîtrise
DOI
10.11606/D.3.2007.tde-03062008-173546
Document
Auteur
Nom complet
Marcos Rogério de Souza
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2007
Directeur
Jury
Wang, Shu Hui (Président)
Agnelli, José Augusto Marcondes
Santa Maria, Luiz Claudio de
Titre en portugais
Blenda de poli (tereftalato de etileno) com polietileno de baixa densidade.
Mots-clés en portugais
Blendas poliméricas (preparação; propriedades)
Resumé en portugais
Neste Trabalho foi preparada e estudada a blenda de poli(tereftalato de etileno) (PET) com polietileno de baixa densidade (PEBD). Esta blenda apresenta interesse científico e tecnológico decorrente da possibilidade de associar as propriedades de resistência térmica e elevado módulo de elasticidade do PET à boa resistência à fratura e à flexibilidade a baixas temperaturas do PEBD. Duas séries de misturas contendo diferentes proporções de PET:PEBD foram preparadas através de mistura em fusão numa extrusora dupla-rosca, contendo como agente compatibilizante poli(etileno-butileno)-bloco-poliestireno (produto comercial) ou poli(etileno-butileno)-bloco-poliestireno sulfonado (produto sintetizado), respectivamente, na proporção de 0 a 6 %. O agente compatibilizante poli(etilenobutileno)- bloco-poliestireno sulfonado foi preparado neste Trabalho a partir do poli(etileno-butileno)-bloco-poliestireno. Todas as misturas preparadas foram caracterizadas quanto às suas propriedades mecânicas através de ensaios de impacto e de tração. As superfícies de fratura criogênica das misturas foram observadas através de microscopia eletrônica de varrredura para caracterização da sua textura. As blendas apresentaram valores de módulo de Young intermediários àqueles observados para o PET (3,54 GPa) e PEBD (110 MPa), entre 1,32 GPa e 2,84 GPa. O mesmo foi observado para a resistência à tração na ruptura, cujos valores das blendas variaram de 13,3 MPa a 33,9 MPa, comparados com 59,6 MPa e e 0,49 MPa para PET e PEBD, respectivamente.
Titre en anglais
Blend of poli(terephalate ethylene) with low density poliethylene.
Mots-clés en anglais
Blend
Chemical modification
LDPE
PET
Poliethylene
SEBS
Resumé en anglais
In these work blends of poly(ethylene tereftalate) (PET) and low density polyethylene (LDPE) were prepared and studied. The PET/PEBD blend presents scientific and technological interests due to the possibility of combining the high thermal stability and high elasticity modulus of PET with the fracture resistance and low temperature flexibility of LDPE. Two series of PET:LDPE blends with different relative proportions were prepared by melting mixture in a twin-screw extruder having as compatibilizing agent poly(ethylene-butylene)-block-polystyrene (commercial product) or sulfonated poly(ethylene-butylene)-block-polystyrene (synthesized product), respectively, in the range 0-6 %. The compatibilizing agent sulfonated poly(ethylene-butylene)-blockpolystyrene was prepared in this work from poly(ethylene-butylene)-blockpolystyrene. The mechanical properties of the blends were characterized by impact resistance tests and extensional tension tests. Textural analysis of blends was performed by observing their cryogenically fractured surfaces were characterized by scanning electron microscopy. The blends presented Young modulus values between those observed for PET (3.54 GPa) and LDPE (110 MPa), in the range from 1.32 GPa to 2.84 GPa. The same behavior was observed for the tensile strength, which values varied from 13.3 MPa to 33.9 MPa, compared to 59.6 MPa and 0.49 MPa for PET and LDPE, respectively.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2008-07-03
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.