Tese de Doutorado
DOI
10.11606/T.3.2012.tde-03072013-112618
Documento
Autor
Nome completo
Denilson Jose Marcolino de Aguiar
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2012
Orientador
Banca examinadora
Padilha, Angelo Fernando (Presidente)
Hupalo, Marcio Ferreira
Lima, Nelson Batista de
Martorano, Marcelo de Aquino
Silva, Manoel Ribeiro da
Título em português
Estudo da formação e reversão de martensita induzida por deformação na austenita de dois aços inoxidáveis dúplex.
Palavras-chave em português
Aço inoxidável duplex e super duplex
Encruamento
Martensita induzida por deformação
Recristalização
Recuperação
Resumo em português
No presente trabalho foram estudados os fenômenos de encruamento e, principalmente, a formação e reversão da martensita alfa-linha (a', cúbica de corpo centrado, CCC, ferromagnética) induzida por deformação em um aço inoxidável dúplex UNS S31803 e um super dúplex UNS S32520. Inicialmente, as microestruturas dos dois materiais na condição solubilizada foram caracterizadas com auxílio de várias técnicas complementares de análise microestrutural. Foram determinadas fração volumétrica, estrutura cristalina, composição química, tamanho e morfologia das duas fases (ferrita e austenita). Posteriormente, os dois aços foram deformados por dois métodos: a laminação a frio, dividida em vários estágios, com menores graus de deformação e a limagem, sendo que o cavaco limado resultante apresenta altos graus de deformação. Algumas amostras deformadas foram recozidas. Os fenômenos de encruamento, formação e reversão de martensita induzida por deformação na austenita, recuperação, recristalização da austenita e da ferrita no cavaco limado foram estudados predominantemente por difratometria de raios X e usando o método de Rietveld. A difratometria de raios X também foi utilizada para determinação das microdeformações residuais e tamanhos de cristalito (subgrão), calculadas a partir do alargamento dos picos de difração causado pelas deformações. Desta forma, puderam-se comparar os níveis de deformação da laminação e limagem. Qualitativamente, a formação e reversão da martensita induzida por deformação também foi estudada por meio de medidas magnéticas utilizando-se dados de saturação magnética das curvas de histerese obtidas com o auxílio de um magnetômetro de amostra vibrante. Observou-se que para o aço inoxidável dúplex, tanto a laminação quanto a limagem causaram a formação de martensita induzida por deformação e para o aço inoxidável super dúplex, apenas a limagem promoveu essa transformação. Em comparação com o aço dúplex, o aço super dúplex apresentou maior resistência à formação de martensita induzida por deformação, pois apresenta uma austenita mais rica em nitrogênio e uma maior propensão à formação de fase sigma durante o recozimento, pois apresenta uma ferrita mais rica em cromo e nitrogênio.
Título em inglês
The study of formation and reversion of the strain induced alpha-prime martensite in duplex and super duplex stainless steels
Palavras-chave em inglês
Duplex and super duplex stainless steel
Recovery
Recrystallization
Strain hardening
Strain induced martensite
Resumo em inglês
In the present work the phenomena of strain hardening, formation and reversion of the strain induced alpha-prime martensite (a', body centered cubic, BCC, Ferromagnetic) in an UNS S31803 duplex and UNS S32520 super duplex stainless steels have been studied. Firstly, the microstructures of both materials in the solution annealed condition were characterized with the aid of several microstructural analysis complementary techniques. The volume fraction, crystalline structure, chemical composition, size and morphology of the two phases (ferrite and austenite) have been determined. Further, both steels were deformed by two methods: cold rolling, divided into several stages, with lower strain levels than filing, which the chips resulting had higher strain levels. The phenomena of strain hardening, formation and reversion of strain induced martensite in the austenite phase, recovery and recrystallization of austenite and ferrite phases have been studied, mainly using X-ray diffraction and the Rietveld method. X-ray diffraction was also used to determine the residual microstrain and crystallite size (sub grain), calculated from the diffraction peak broadening caused by straining. Thus, the levels of cold rolling and filing strains could be compared. Qualitatively, the formation and reversion of strain induced martensite was also studied by magnetic measurements using data from magnetic saturation of hysteresis curves obtained with the aid of a vibrating sample magnetometer. It has been observed that for the duplex stainless steel, both filing as well as cold rolling promoted strain induced martensite. On the other hand, for the super duplex stainless steel, just filing promoted this transformation. In the comparing with duplex, the super duplex stainless steel austenite is more stable that is why is richer in nitrogen, so, the strain induced martensite formation is more difficult. The easier sigma phase precipitation during annealing as well in the super duplex stainless steel is due higher levels of chrome and molybdenum than the duplex stainless steel.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2013-07-04
 
AVISO: O material descrito abaixo refere-se a trabalhos decorrentes desta tese ou dissertação. O conteúdo desses trabalhos é de inteira responsabilidade do autor da tese ou dissertação.
  • Padilha, Angelo Fernando, Aguiar, D.J.M., and Plaut, R.L. Duplex Stainless Steels: A Dozen of Significant Phase Transformations [doi:10.4028/www.scientific.net/DDF.322.163]. Defect and Diffusion Forum [online], 2012, vol. 322, p. 163-174.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2020. Todos os direitos reservados.