Doctoral Thesis
DOI
10.11606/T.3.2018.tde-03102018-085529
Document
Author
Full name
Gonçalo Siqueira
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2018
Supervisor
Committee
Wiebeck, Hélio (President)
Yee, Márcio
Esper, Fábio José
Oliveira, José Mauro Diniz
Silva, Leonardo Gondim de Andrade e
Title in Portuguese
Desenvolvimento com tinta de nanocarga para aplicação nos estudos da velocidade de corrosão.
Keywords in Portuguese
Corrosão
Dióxido de silício
EIS
Óxido de zinco
Processo de irradiação
SVET
Tintas
Vermiculita
Abstract in Portuguese
A corrosão é um dos problemas mais relevantes que afronta a indústria atual, representa mais de 25% do investimento destinado para reparos ou troca de equipamentos com falhas por problemas do ataque corrosivo. Neste panorama nos últimos anos houve um grande aumento no desenvolvimento de novas tecnologias para proteção das estruturas, por outro lado o aço ABTN 1020 é um dos materiais mais usados na indústria principalmente em ambientes contendo cloreto. A sua utilização não é recomendada pelas altas taxas de corrosão, sendo necessário à adoção de pintura como meio de proteção. Este trabalho investigou a resistência à corrosão de uma pintura em meios contendo cloreto cuja composição da matriz foi resina uretânica (PU) e diferentes cargas a base de SiO2 e ZnO em diversas concentrações, sendo avaliadas mediante técnicas de Impedância Eletroquímica- EIS e de varredura com elétrodo vibratório SVET. Verificou-se que a espectroscopia e SVET também fornecem informação suficiente relativo ao desgaste e a possível ação da corrosão, sendo assim foi evidenciado que pintura com carga a base de SiO2 que tem melhor resistência à corrosão em meios contendo cloreto. Em outra análise quando comparados com a carga de ZnO pintura com irradiação, observou-se que houve um aumento na aderência da pintura ao metal base, fornecendo uniformidade e maior proteção anticorrosiva, assim foram determinados parâmetros que podem aplicações na indústria.
Title in English
Development with nanocarga paint for application in corrosion speed studies.
Keywords in English
EIS
Irradiation process
Silicon dioxide
SVET
Zinc oxide
Abstract in English
Corrosion is one of the most important problems facing today's industry, representing more than 25% of the investment destined for repairs or exchange of equipment with failures due to corrosive attack problems. In this panorama in recent years there has been a great increase in the development of new technologies for protection of structures, on the other hand the steel ABTN 1020 is one of the materials most used in the industry mainly in environments containing chloride. Its use is not recommended due to the high corrosion rates, and it is necessary to adopt painting as a means of protection. This work investigated the corrosion resistance of a paint in chloride-containing media whose urethane resin (PU) composition and different SiO2 and ZnO-based loads were evaluated in various concentrations and evaluated by Electrochemical Impedance-EIS and scanning with vibrating electrode SVET. It was verified that the spectroscopy and SVET also provide sufficient information regarding the wear and the possible action of the corrosion, thus it was evidenced that paint with charge based on SiO2 that has better resistance to corrosion in media containing chloride. In another analysis when compared with the ZnO charge with irradiation paint, it was observed that there was an increase in the adhesion of the paint to the base metal, providing uniformity and greater anticorrosive protection, thus determined parameters that can be applied in the industry.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2018-10-05
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.