Tesis Doctoral
DOI
10.11606/T.3.2018.tde-03102018-085529
Documento
Autor
Nombre completo
Gonçalo Siqueira
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2018
Director
Tribunal
Wiebeck, Hélio (Presidente)
Yee, Márcio
Esper, Fábio José
Oliveira, José Mauro Diniz
Silva, Leonardo Gondim de Andrade e
Título en portugués
Desenvolvimento com tinta de nanocarga para aplicação nos estudos da velocidade de corrosão.
Palabras clave en portugués
Corrosão
Dióxido de silício
EIS
Óxido de zinco
Processo de irradiação
SVET
Tintas
Vermiculita
Resumen en portugués
A corrosão é um dos problemas mais relevantes que afronta a indústria atual, representa mais de 25% do investimento destinado para reparos ou troca de equipamentos com falhas por problemas do ataque corrosivo. Neste panorama nos últimos anos houve um grande aumento no desenvolvimento de novas tecnologias para proteção das estruturas, por outro lado o aço ABTN 1020 é um dos materiais mais usados na indústria principalmente em ambientes contendo cloreto. A sua utilização não é recomendada pelas altas taxas de corrosão, sendo necessário à adoção de pintura como meio de proteção. Este trabalho investigou a resistência à corrosão de uma pintura em meios contendo cloreto cuja composição da matriz foi resina uretânica (PU) e diferentes cargas a base de SiO2 e ZnO em diversas concentrações, sendo avaliadas mediante técnicas de Impedância Eletroquímica- EIS e de varredura com elétrodo vibratório SVET. Verificou-se que a espectroscopia e SVET também fornecem informação suficiente relativo ao desgaste e a possível ação da corrosão, sendo assim foi evidenciado que pintura com carga a base de SiO2 que tem melhor resistência à corrosão em meios contendo cloreto. Em outra análise quando comparados com a carga de ZnO pintura com irradiação, observou-se que houve um aumento na aderência da pintura ao metal base, fornecendo uniformidade e maior proteção anticorrosiva, assim foram determinados parâmetros que podem aplicações na indústria.
Título en inglés
Development with nanocarga paint for application in corrosion speed studies.
Palabras clave en inglés
EIS
Irradiation process
Silicon dioxide
SVET
Zinc oxide
Resumen en inglés
Corrosion is one of the most important problems facing today's industry, representing more than 25% of the investment destined for repairs or exchange of equipment with failures due to corrosive attack problems. In this panorama in recent years there has been a great increase in the development of new technologies for protection of structures, on the other hand the steel ABTN 1020 is one of the materials most used in the industry mainly in environments containing chloride. Its use is not recommended due to the high corrosion rates, and it is necessary to adopt painting as a means of protection. This work investigated the corrosion resistance of a paint in chloride-containing media whose urethane resin (PU) composition and different SiO2 and ZnO-based loads were evaluated in various concentrations and evaluated by Electrochemical Impedance-EIS and scanning with vibrating electrode SVET. It was verified that the spectroscopy and SVET also provide sufficient information regarding the wear and the possible action of the corrosion, thus it was evidenced that paint with charge based on SiO2 that has better resistance to corrosion in media containing chloride. In another analysis when compared with the ZnO charge with irradiation paint, it was observed that there was an increase in the adhesion of the paint to the base metal, providing uniformity and greater anticorrosive protection, thus determined parameters that can be applied in the industry.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2018-10-05
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.