Disertación de Maestría
DOI
10.11606/D.3.2018.tde-04102018-081012
Documento
Autor
Nombre completo
Raphael Cons Andrades
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2018
Director
Tribunal
Diaz, Francisco Rolando Valenzuela (Presidente)
Júnior, Antônio Hortêncio Munhoz
Neves, Roberto de Freitas
Título en portugués
Sí­ntese de zeólita A e aplicação em adsorção de metais pesados.
Palabras clave en portugués
Adsorção
Caulim
Metais pesados
Síntese hidrotermal
Zeólita A
Resumen en portugués
Este trabalho objetivou estudar a síntese de zeólita NaA sob condições hidrotérmicas e aplicála na adsorção de metais pesados. Para a síntese de zeólita NaA, caulim do município de Ipixuna, Pará, foi calcinado a 700 °C por 3 horas para obtenção de metacaulim e usado como fonte de sílica e alumina. Para efeito de comparação, cloreto de alumínio e metassilicato de sódio também foram utilizados na síntese de zeólitas como precursores de Si e Al. A influência da alcalinidade na síntese dos produtos zeolíticos foi avaliada utilizando-se diferentes concentrações de NaOH. Todas as sínteses foram realizadas a 110 °C em autoclaves. Visando à compreensão da influência do tempo na quantidade e tipo de fase formada, foram realizadas sínteses com diferentes tempos de cristalização. Os produtos de reação foram caracterizados por difração de raios X, espectroscopia na região do infravermelho, análise termogravimétrica, análise térmica diferencial, microscopia eletrônica de varredura e adsorção de nitrogênio para cálculo de área específica pelo método BET. A amostra que apresentou maior proporção de zeólita NaA foi utilizada como adsorvente em soluções de Cu2+, Ni2+ e Cd2+ com concentrações iniciais de 25 a 400 mg/L. A concentração de equilíbrio desses metais, após remoção pela zeólita NaA, foi determinada por espectrofotometria de absorção atômica. Os resultados mostraram que o aumento da alcalinidade e do tempo de cristalização favoreceu a obtenção de sodalita, uma fase zeolítica concorrente à Zeólita A, nos produtos de síntese. A zeólita NaA provou ser um excelente adsorvente para remoção dos metais analisados, apresentando uma capacidade de adsorção máxima de aproximadamente 79, 65 e 32 mg/g para Cd2+, Cu2+ e Ni2+, respectivamente. O modelo de isoterma de adsorção que melhor descreveu a remoção de metais pela zeólita NaA foi o de Langmuir.
Título en inglés
Synthesis of Zeolite A and application in adsorption of heavy metals.
Palabras clave en inglés
Adsorption
Heavy metals
Hydrothermal synthesis
Kaolin
Zeolite A
Resumen en inglés
The aim of this work was to study the synthesis of zeolite NaA under hydrothermal conditions and use it as adsorbent of heavy metals. To synthesize zeolite NaA, kaolin from the city of Ipixuna, Pará, was calcined at 700 °C for 3 hours and used as source of silica and alumina. For comparison purposes, aluminum chloride and sodium metasilicate were also used in the synthesis of zeolites as precursors of Si and Al. The influence of alkalinity on the synthesis of the zeolitic products was evaluated using different NaOH concentrations. All the syntheses were performed at 110 °C by autoclaving. To understand the influence of time on the type and relative amount of the obtained phases, syntheses with different crystallization times were carried out. The reaction products were characterized by means of X-ray diffraction, infrared spectroscopy, thermogravimetric analysis, thermal differential analysis, scanning electron microscopy and nitrogen adsorption for calculating surface area by the BET method. One of the samples, which exhibited the highest content of zeolite NaA, was used as adsorbent of Cu2+, Ni2+ and Cd2+ solutions with initial concentrations ranging from 25 to 400 mg/L. The equilibrium concentration of these heavy metals, after removal by zeolite NaA, was determined by atomic absorption spectrophotometry. The results showed that increasing alkalinity of the reaction medium led to the formation of sodalite, a concurrent zeolitic phase, in the products. Zeolite NaA turned out to be an excellent adsorbent for removing heavy metals, with an adsorption capacity of 79, 65 and 32 mg/g for Cu2+, Cd2+ and Ni2+, respectively. The Langmuir isotherm model was the most appropriate to describe the removal of metals by zeolite A.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2018-10-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.