Master's Dissertation
DOI
10.11606/D.3.2016.tde-05102016-092735
Document
Author
Full name
Estevan Helio Panisello Candel
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2016
Supervisor
Committee
Brandi, Sérgio Duarte (President)
Aoki, Idalina Vieira
Souza, Paulo Cézar Rioli Duarte de
Title in Portuguese
Soldagem dos aços inoxidáveis superduplex UNS S32750 e UNS S32760.
Keywords in Portuguese
Aço inoxidável
Arame tubular (MCAW)
Soldagem eletrônica
Superduplex
Tubulações
Abstract in Portuguese
O objetivo deste trabalho é viabilizar o uso conjunto, em um mesmo sistema de tubulação, na indústria de óleo e gás, dos aços inoxidáveis superduplex UNS S32750 e UNS S32760. Atualmente as especificações de projeto limitam o uso de um ou outro para um dado sistema, implicando em menor flexibilidade de fornecimento e maiores custos. Adicionalmente será avaliado o processo de soldagem automatizado com arame tubular com matriz metálica (metal cored) e com proteção gasosa. Este processo de soldagem possui grande produtividade e rendimento. Foram estudadas a resistência à corrosão, a resistência mecânica e possíveis danos causados à microestrutura do metal de solda e das zonas afetadas pelo calor (ZAC) dos aços inoxidáveis superduplex UNS S32750 e UNS S32760. A junta foi realizada com chanfro em meio "V", com geometria de 300 mm por 200 mm por 6,35 mm e com os seguintes parâmetros de soldagem: tensão de 25 V, corrente de 150 A, velocidade de soldagem de 6,35 mm/s, velocidade de alimentação do arame de 135 mm/s e distância de trabalho de 20 mm. As juntas foram caracterizadas por microscopia óptica, eletrônica de varredura, ensaio de tração, ensaio de dobramento, ensaio Charpy V a - 46 °C e ensaio de corrosão segundo a norma ASTM G48. A base para os critérios de aprovação será o disposto normativo da Norsok Standard M-601, Welding and inspection of piping, na sua mais recente edição (2008). Os resultados mostraram que não existem diferenças significativas entre as soldagens similares e dissimilares com relação às propriedades testadas.
Title in English
UNS S32750 and UNS S32760 superduplex stainless steel welding.
Keywords in English
Metal Cored Arc Welding (MCAW)
Pipelines
Superduplex stainless steels
Weldability
Abstract in English
The objective of this work is to enable the use in the same piping system, used in the oil and gas industry, of UNS S32750 and UNS S32760 superduplex stainless steels. Currently, the design specifications limit the use of one or the other for a given system, resulting in less flexibility in supply and higher costs. Additionally, it will be evaluated automated welding process with metal cored using a shielding gas. This welding process has high productivity and efficiency. It was studied corrosion resistance, mechanical strength and possible damage to the weld metal microstructure and heat affected zones (HAZ) of stainless steels superduplex UNS S32750 and UNS S32760. The joint was welded using a half "V" bevel geometry, with 300 mm by 200 mm by 6.35 mm and the following welding parameters: voltage 25 V, current 150 A, welding speed of 6.35 mm/s, wire feed speed of 135 mm/s and 20 mm working distance. The joints were characterized by optical microscopy, scanning electron microscopy, tensile test, bending test, Charpy V test at - 46 °C and corrosion test according to ASTM G48. The basis for the criteria for approval is the normative provisions of Norsok Standard M-601, Welding and inspection of piping in its latest edition (2008). The results showed that there are no significant differences between similar and dissimilar welds with respect to the tested properties.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2016-10-05
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.