Mémoire de Maîtrise
DOI
10.11606/D.3.2016.tde-05102016-092735
Document
Auteur
Nom complet
Estevan Helio Panisello Candel
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2016
Directeur
Jury
Brandi, Sérgio Duarte (Président)
Aoki, Idalina Vieira
Souza, Paulo Cézar Rioli Duarte de
Titre en portugais
Soldagem dos aços inoxidáveis superduplex UNS S32750 e UNS S32760.
Mots-clés en portugais
Aço inoxidável
Arame tubular (MCAW)
Soldagem eletrônica
Superduplex
Tubulações
Resumé en portugais
O objetivo deste trabalho é viabilizar o uso conjunto, em um mesmo sistema de tubulação, na indústria de óleo e gás, dos aços inoxidáveis superduplex UNS S32750 e UNS S32760. Atualmente as especificações de projeto limitam o uso de um ou outro para um dado sistema, implicando em menor flexibilidade de fornecimento e maiores custos. Adicionalmente será avaliado o processo de soldagem automatizado com arame tubular com matriz metálica (metal cored) e com proteção gasosa. Este processo de soldagem possui grande produtividade e rendimento. Foram estudadas a resistência à corrosão, a resistência mecânica e possíveis danos causados à microestrutura do metal de solda e das zonas afetadas pelo calor (ZAC) dos aços inoxidáveis superduplex UNS S32750 e UNS S32760. A junta foi realizada com chanfro em meio "V", com geometria de 300 mm por 200 mm por 6,35 mm e com os seguintes parâmetros de soldagem: tensão de 25 V, corrente de 150 A, velocidade de soldagem de 6,35 mm/s, velocidade de alimentação do arame de 135 mm/s e distância de trabalho de 20 mm. As juntas foram caracterizadas por microscopia óptica, eletrônica de varredura, ensaio de tração, ensaio de dobramento, ensaio Charpy V a - 46 °C e ensaio de corrosão segundo a norma ASTM G48. A base para os critérios de aprovação será o disposto normativo da Norsok Standard M-601, Welding and inspection of piping, na sua mais recente edição (2008). Os resultados mostraram que não existem diferenças significativas entre as soldagens similares e dissimilares com relação às propriedades testadas.
Titre en anglais
UNS S32750 and UNS S32760 superduplex stainless steel welding.
Mots-clés en anglais
Metal Cored Arc Welding (MCAW)
Pipelines
Superduplex stainless steels
Weldability
Resumé en anglais
The objective of this work is to enable the use in the same piping system, used in the oil and gas industry, of UNS S32750 and UNS S32760 superduplex stainless steels. Currently, the design specifications limit the use of one or the other for a given system, resulting in less flexibility in supply and higher costs. Additionally, it will be evaluated automated welding process with metal cored using a shielding gas. This welding process has high productivity and efficiency. It was studied corrosion resistance, mechanical strength and possible damage to the weld metal microstructure and heat affected zones (HAZ) of stainless steels superduplex UNS S32750 and UNS S32760. The joint was welded using a half "V" bevel geometry, with 300 mm by 200 mm by 6.35 mm and the following welding parameters: voltage 25 V, current 150 A, welding speed of 6.35 mm/s, wire feed speed of 135 mm/s and 20 mm working distance. The joints were characterized by optical microscopy, scanning electron microscopy, tensile test, bending test, Charpy V test at - 46 °C and corrosion test according to ASTM G48. The basis for the criteria for approval is the normative provisions of Norsok Standard M-601, Welding and inspection of piping in its latest edition (2008). The results showed that there are no significant differences between similar and dissimilar welds with respect to the tested properties.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2016-10-05
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.