Mémoire de Maîtrise
DOI
10.11606/D.3.2017.tde-06122017-142418
Document
Auteur
Nom complet
Vanessa Tiemi Kimura
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2017
Directeur
Jury
Hui, Wang Shu (Président)
Silva, Ana Neilde Rodrigues da
Zanin, Maria Helena Ambrosio
Titre en portugais
Produção e caracterização de scaffolds de diferentes espessuras obtidos por eletrofiação de nanofibra polimérica e proteína.
Mots-clés en portugais
Engenharia tecidual
Materiais nanoestruturados
Resumé en portugais
A engenharia tecidual visa repor, reparar ou ajudar a regenerar tecidos e órgãos danificados por meio da combinação de biomateriais, biomoléculas e células. Scaffolds de nanofibras biodegradáveis mimetizam a matriz extracelular natural fornecendo uma estrutura ideal para o crescimento celular. Blendas de policaprolactona (PCL) e gelatina são biodegradáveis e proporcionam uma combinação de boas propriedades mecânicas, do PCL, com a hidrofilicidade e caráter que promove a adesão celular, da gelatina. Neste contexto, o objetivo deste trabalho é avaliar a importância das diferentes espessuras de scaffolds eletrofiados em relação às suas propriedades principais. Quatro conjuntos de scaffolds de PCL/gelatina com diferentes espessuras foram produzidos sob as mesmas condições apenas aumentando o tempo de duração do processo de eletrofiação. Os resultados indicam que as espessuras aumentaram proporcionalmente ao tempo de eletrofiação, variando de 100 nm a 300 nm nos períodos de 1 a 3 horas, enquanto a densidade aparente e a porosidade mantiveram-se constantes. As micrografias das membranas revelaram fibras lisas com diâmetros maiores para os scaffolds de menor espessura, e fibras irregulares com diâmetros menores e regiões fundidas ou ligadas para os scaffolds de maior espessura. Além disso, o aumento da espessura melhorou a resistência mecânica e a molhabilidade dos scaffolds. A esterilização por peróxido de hidrogênio não modificou quimicamente a composição das membranas de PCL/gelatina, embora algumas amostras tenham se deformado. As membranas também apresentaram bons resultados de citotoxicidade, melhorando a viabilidade celular, apesar desses valores diminuírem minimamente para os scaffolds de maior espessura, provavelmente devido à maior quantidade de PCL. O teste de adesão não foi conclusivo e deverá ser repetido.
Titre en anglais
Production and characterization of electrospun polymeric-protein nanofiber scaffolds with different thicknesses.
Mots-clés en anglais
Biomaterials
Electrospinning
Nanofibers
Scaffold
Tissue engineering
Resumé en anglais
Tissue engineering aims to replace, repair, or helping regenerate damaged tissues and organs through the combination of biomaterials, biomolecules and cells. Biodegradable nanofibrous scaffolds mimic the natural extracellular matrix providing an ideal structure to cellular growth. Blends of polycaprolactone (PCL) and gelatin are biodegradable and provide a combination of good mechanical properties, from PCL, with the hydrophilicity and cell adhesion promoter character, from gelatin. The aim of this work was to evaluate the importance of the thickness of electrospun scaffolds on their key properties. Four sets of PCL/gelatin scaffolds with different thicknesses were produced under the same conditions by simply increasing the time length of electrospinning process. Results indicate that the thickness increases proportionally to the electrospinning time, varying from 100 nm to 300 nm in periods of 1 to 3 hours, while the apparent density and porosity remained constant. Micrographs from the nonwoven mats revealed smooth fibers with larger diameters in the thinner scaffold, and irregular fibers with smaller diameters and molten or bonded regions as the thickness increased. Furthermore, the increase of thickness improved mechanical resistance and wettability of the scaffolds. Plasma sterilization did not modify chemical composition of PCL/gelatin membranes, although some samples have been deformed. Membranes also presented good results for cytotoxicity, improving cell viability, despite these values decreased minimally to the thicker scaffolds, probably due to the higher amount of PCL. Adhesion test was not conclusive and might be repeat.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2017-12-06
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.