Disertación de Maestría
DOI
10.11606/D.3.2019.tde-08042019-085517
Documento
Autor
Nombre completo
Antonio Augusto Gorni
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 1990
Director
Tribunal
Vieira, Renato Rocha (Presidente)
Falleiros, Ivan Gilberto Sandoval
Guimaraes, Jose Roberto Costa
Título en portugués
Efeito da temperatura de acabamento e velocidade de resfriamento sobre a microestrutura e propriedades mecânicas de um aço bifásico.
Palabras clave en portugués
Aço
Resumen en portugués
Chapas de aço bifásico ("dual phase") se caracterizam por apresentar microestrutura composta de matriz de ferrita poligonal com 15 a 20% de martensita dispersa, o que lhes confere alta resistência mecânica aliada a boa conformabilidade. Este tipo de material pode ser obtido diretamente após a laminação a quente através da aplicação de tratamento termomecânico. O objetivo deste trabalho foi estudar o efeito da temperatura de acabamento e velocidade de resfriamento sobre o desenvolvimento da microestrutura e propriedades mecânicas de um aço bifásico ao Mn-Si-Cr-Mo próprio para laminação a quente. A técnica experimental consistiu de ensaio de laminação a quente em cinco passes, em que foi variada a temperatura de acabamento, ou de fim de laminação. A seguir os corpos de prova foram resfriados em meios com diferentes severidades de têmpera. Procedeu-se então à análise das amostras através de metalografia quantitativa e ensaio de tração. Os resultados mostraram que quando o resfriamento foi feito de modo direto a velocidade de resfriamento é o parâmetro mais importante na determinação da microestrutura e propriedade4 mecânicas, cabendo à temperatura de acabamento um papel secundário. No caso das amostras submetidas a resfriamento escalonado a variável que influenciou decisivamente as propriedades mecânicas do material foi a temperatura em que a têmpera foi interrompida.
Título en inglés
Sem título em inglês
Palabras clave en inglés
Steel
Resumen en inglés
Dual phase steel strips show a microstructure that consists of a soft polygonal ferrite matrix with 15 to 20% of hard martensite dispersed on it, which grants high strength and good cold formability to this product. This kind of steel can be produced direct from the rolling heat through the application of a thermomechanical treatment compatible with the chemical composition of the steel. The aim of this work was to study the effect of the colling finish temperature and coolong rate on the development of the microstructure and mechanical properties of a Mn-Si-Cr-Mo dual-phase steel suitable for hot rolling. The experimental technique comprised a Five-pass hot rolling Schedule on a laboratory rollong Mill using different finish temperatures. Then the samples were copied in media with different quench severities. The samples thus obtained were analysed through quantitative metallography and tension testing. The results obtained showed that in the samples directly quenched the cooling rate is the capital parameter for the determination of the microstructure and mechanical properties, whereas the finish temperature plays a secondary role. When the samples were submitted to interrupted quenching the variable that decisively influenced the mechanical properties was the temperature on which the quench was interrupted.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2019-04-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.