Master's Dissertation
DOI
10.11606/D.3.2008.tde-09022009-160616
Document
Author
Full name
Fabio Stagetti
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2008
Supervisor
Committee
Padilha, Angelo Fernando (President)
Batalha, Gilmar Ferreira
Sandim, Hugo Ricardo Zschommler
Title in Portuguese
Encruamento e recristalização dos aços rápidos AISI M2 e ABC III: um estudo comparativo.
Keywords in Portuguese
Aço ferramenta
Aço rápido
Metalurgia física
Recristalização
Abstract in Portuguese
O objetivo deste trabalho é realizar um estudo comparativo da recristalização de dois aços rápidos, AISI M2 (Werkstoffnummer 1.3343) e ABC III (Werkstoffnummer 1.3333), após o encruamento resultante do processo de laminação a frio de chapas planas utilizadas para a confecção de serras fitas. Estudar a recristalização estática nesta classe de aços é relevante, pois eles freqüentemente são laminados a frio e recozidos na etapa final de processamento, antes da confecção da peça ou componente. Inicialmente, foi realizada a caracterização das amostras no estado como recebido, ou seja ''laminado a quente''. A caracterização envolveu análise química, ensaios mecânicos, microscopia óptica, microscopia eletrônica de varredura, medidas de dureza e dilatometria. Em seguida, as amostras sofreram deformação a frio da ordem de até 50% de redução em espessura para determinação das curvas de endurecimento por deformação. Amostras com 25% de redução foram recozidas entre 100ºC e 750ºC, durante 1 hora e os resultados de dureza foram utilizadas para determinar as curvas isócronas de amolecimento. Amostras com 25% redução foram recozidas entre 600ºC e 750ºC, entre 15 e 480 minutos para cada uma das temperaturas, para determinação curvas isotérmicas de amolecimento. Resultados da análise microestrutural mostraram que o aço rápido AISI M2 apresenta uma distribuição mais homogênea de carbonetos. Esses carbonetos são mais finos em relação aos do aço ABC III, que apresenta uma distribuição mais heterogênea. Os dois aços apresentaram curvas muito similares de endurecimento por deformação. Após recozimento das amostras encruadas, foi verificado que o aço AISI M2 apresenta recuperação e recristalização levemente mais rápidas quando comparado com o ABC III. Ainda na etapa de recuperação e antes da recristalização, notou-se nos dois aços um pequeno aumento de dureza, principalmente entre 30 e 60 minutos de recozimento, na faixa de 650 ºC e 700ºC. Utilizando-se análises por difração de elétrons retroespalhados (microtextura e mesotextura) observou-se que o aço ABC III apresenta maior resistência para a recristalização se completar que o aço AISI M2.
Title in English
Work hardening and recrystallization of high speed AISI M2 and ABC III: a comparative study.
Keywords in English
High speed steel
Physical metallurgy
Recrystallization
Tool steel
Abstract in English
This work aims at the comparative study of the recrystallization of two high-speed steels, namely AISI M2 (Werkstoffnummer 1.3343) and ABC III (Werkstoffnummer 1.3333), hardened by cold rolling of sheets employed in the production of band saws. Studying static recrystallization in this class of steels is relevant, since frequently they are cold rolled and annealed in their final processing stage, prior to the actual work piece manufacturing. Initially, samples have been characterized in the as-received condition, i.e. hot rolled. Characterization involved chemical analysis, tensile testing, optical metallography, scanning electron microscopy, hardness measurements and dilatometry. Following, samples have been cold worked with a 50% thickness reduction in order to evaluate the cold work hardening curves. Samples with 25% reduction have been annealed at temperatures in the 100oC to 750oC range, for one hour and hardness results have been used to determine the isochronous softening curves. Samples with 25% reduction have been annealed between 600 oC and 750oC for 15 to 480 minutes, for each one of the temperatures, to determine the isothermal softening curves. The microstructural analysis has shown that the AISI M2 steel presents a homogeneous carbide distribution. These carbides were fine when compared to those of the ABCIII steel that presented a heterogeneous distribution. Both steels presented similar work-hardening curves. After annealing the cold worked samples, it has been observed that the AISI M2 steel presented a slightly faster recovery and recrystallization than the ABCIII steel. Still in the recovery stage, prior to recrystallization, both steels showed a small hardness increase, mainly on annealing during 30 to 60 minutes in the 650oC to 700oC temperature range. Using electron backscattered diffraction analysis (microtexture and mesotexture) it has been observed that the ABCIII steel presented higher resistance to complete recrystallization than the AISI M2 steel.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Dissertacao_final.pdf (10.66 Mbytes)
Publishing Date
2009-02-20
 
WARNING: The material described below relates to works resulting from this thesis or dissertation. The contents of these works are the author's responsibility.
  • STAGETTI, Fábio, et al. Estudo comparativo do encruamento e da recristalização dos aços rápidos M2 e ABC III. In 45º Seminário de Laminação, Ipojuca-Porto de Galinhas, PE, 2008. Anais do 45º Seminário de Laminação da ABM.São Paulo, SP : ABM, 2008.