Master's Dissertation
DOI
10.11606/D.3.2006.tde-09052007-162851
Document
Author
Full name
André Luis de Carvalho
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2006
Supervisor
Committee
Wiebeck, Hélio (President)
Silva, Leonardo Gondim de Andrade e
Wang, Shu Hui
Title in Portuguese
Avaliação comparativa da interação intermolecular do PMMA em termoformagem.
Keywords in Portuguese
Ligações cruzadas
Plastificante
PMMA
Termoformagem
Abstract in Portuguese
Chapas de poli(metacrilato de metila) podem ser modificadas por meio da adição de um agente promotor de ligações cruzadas e um plastificante objetivando incrementar seu desempenho durante a termoformagem. A interação intermolecular, modificada com a adição de diferentes quantidades de um agente promotor de ligações cruzadas (TEGDMA) e pela presença de um plastificante (DOP) faz com que as macromoléculas sejam ancoradas e afastadas respectivamente. O desenvolvimento deste trabalho objetivou, avaliar as propriedades físicas, mecânicas, térmicas e o processamento via termoformagem para duas diferentes temperaturas de termoformagem em um molde cilíndrico, a uma mesma taxa de deformação e determinado a influência da formulação, para cinco chapas que se diferenciaram nas quantidades de TEGDMA e uma quantidade fixada de DOP para duas das formulações. Os resultados mostraram que há incremento na deformação com as modificações introduzidas quando comparado a uma chapa sem adição de TEGDMA ou DOP e as propriedades destas chapas como dureza superficial, módulo de rigidez e temperatura de transição vítrea apresentaram mudanças sensíveis, que caracterizam vantagens no uso dos dois componentes.
Title in English
Evaluation comparison of PMMA intermolecular interaction in thermoforming.
Keywords in English
Cross-link
Plasticizer
PMMA
Thermoforming
Abstract in English
Poly(methyl methacrylate) sheets can be modified adding a cross-linking agent and a plasticizer, to increase performance during thermoforming. The intermolecular interaction modification can be achieved adding different amount of cross-linking agent (TEGDMA) and a plasticizer (DOP). They have an effect on the network polymer system improving the intermolecular interaction and increasing the macromolecular distances, respectively. The aim of this study was to prepare acrylic sheets formulations with differents amounts of TEGDMA and a fixed amount of DOP, and thermoformed using at differents process temperatures and a mould cylinder at the same strain rate. Samples were carried out and their properties physical, mechanical, thermal and thermoformability was characterized. The results have shown strain increases, changes in surface hardness, Young moduli and glass transition temperature, compared to a reference acrylic sheet.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
means that the file can only be accessed inside the Unversity of São Paulo.
Publishing Date
2007-06-05
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.