Disertación de Maestría
DOI
10.11606/D.3.2010.tde-10012011-142919
Documento
Autor
Nombre completo
Victor Bridi Telles
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2010
Director
Tribunal
Tenório, Jorge Alberto Soares (Presidente)
Bernardes, Andréa Moura
Espinosa, Denise Crocce Romano
Título en portugués
Reciclagem da poeira de aciaria elétrica na sinterização de minério de ferro visando a eliminação de zinco.
Palabras clave en portugués
Poeira de aciaria elétrica (PAE)
Reciclagem
Sinterização
Zinco
Resumen en portugués
Este trabalho tem por objetivo estudar o aproveitamento do pó de aciaria elétrica (PAE) na sinterização de minério de ferro visando a eliminação de zinco. Primeiramente, foi feita uma caracterização física e química do resíduo através de análises químicas, granulométricas, morfológicas e de difração de raios-X. O minério de ferro, principal componente do processo de sinterização, foi caracterizado através de análise química, granulométrica e de umidade. Em seguida, foram fabricadas micropelotas de 3,0 a 5,0mm de diâmetro compostas por 70% de PAE e 30% de moinha de coque, que foram classificadas por peneiramento e secas em esfufa. Depois de aglomerado, o resíduo foi incorporado na sinterização de minério de ferro em diferentes proporções, condições de processo e formas de adição (micropelotas, undersize da micropelotização com granulometria entre 1,0 e 2,0mm, ou mistura de PAE e coque em pó). A cada processo de sinterização foram retiradas amostras de sínter, os materiais foram analisados através de Microscópio Eletrônico de Varredura (MEV), macroscopia e análises químicas por espectrofotometria de absorção atômica para verificar o teor de zinco. Amostras de misturas não sinterizadas também foram submetidas a análises químicas para determinar a quantidade inicial de zinco, ou seja, verificar a quantidade de zinco contido na mistura antes do processo de sinterização. Mediante a comparação do teor de zinco das amostras não sinterizadas com os sínteres, foi possível determinar a eliminação de zinco nos ensaios realizados. Aproximadamente 92% de zinco foi eliminado (junto com os gases de saída) com a incorporação de 10% de micropelotas na mistura a sinterizar. Os resultados mostraram que a eliminação do metal no processo é proporcional à relação redutor/resíduo.
Título en inglés
Eletric arc furnace dust recycling in iron ore sintering process aiming zinc removal
Palabras clave en inglés
Electric arc furnace dust (EAFD)
Recycling
Sintering process
Zinc
Resumen en inglés
The aim of this work was to study the use of electric arc furnace dust (EAFD) in iron ore sintering process aiming zinc elimination. Firstly, physical and chemical characterizations of the waste were made using X-ray diffraction, microscopy, chemical and size analyses. Iron ore is the main component of the sintering process, this material was characterized by chemical, size and humidity analyses. After, micropellets composed of EAFD 70% and coke breeze 30% with diameters of 3.0-5.0 mm were produced, then they were dried in kiln and classified by sieving. The pellets were incorporated into the iron ore sintering charge using differents proportions, process conditions and addition forms (micropellets, undersize with diameters of 1.0-2.0 mm, or a mixture of EAFD and coke breeze). Sintered samples were collected in each sintering process. These materials were analyzed by scanning electron microscopy (SEM), macroscopy and chemical analysis using atomic absorption spectrophotometry in order to determine the zinc content. Samples of not sintered mixtures were also characterized by chemical analysis aiming the determination the initial amounts of zinc, i.e. in order to check the zinc amounts present in the mixture before the sintering process. The comparation between the zinc contents of sintered samples and not sintered allowed to determine the elimination of zinc during the experiments. About 92% of zinc was eliminated (along with the output gas) with the incorporation of 10% of micropellet in the sintering mixture. Results showed that the zinc elimination in the process is proportional to the ratio reducer/waste.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2011-04-19
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.